PERENGKAHAN KATALITIK LIMBAH PLASTIK LDPE MENJADI FRAKSI GASOLIN MENGGUNAKAN KATALIS NIKEL TERIMPREGNASI ZEOLIT ALAM

MOH. TAUFIQURROHMAN , Prof. Dr. Karna Wijaya, M.Eng; Mokhammad Fajar Pradipta, S.Si, M.Eng

2018 | Skripsi | S1 KIMIA

Telah dilakukan sintesis katalis Ni/Zeolit Alam untuk hidrorengkah limbah plastik LDPE. Preparasi zeolit dimulai dengan merendam zeolit dengan akuades, lalu direfluks dengan HCl 6M. Selanjutnya zeolit yang sudah teraktivasi diimpregnasi dengan Ni-nitrat menggunakan metode impregnasi basah, sehingga setelah direfluks, dikalsinasi, dan direduksi diperoleh katalis Ni/Zeolit Alam. Tahap berikutnya dilakukan karakterisasi menggunakan XRD, SAA, AAS, FTIR, TEM, dan TG/DTA. Uji aktivitas katalis Ni/Zeolit Alam dilakukan menggunakan reaktor stainless steel sistem semi-batch untuk hidrorengkah limbah plastik LDPE pada suhu hingga 200 oC. Produk cair hasil hidrorengkah dianalisis menggunakan GC-MS. Hasil penelitian menunjukkan bahwa jumlah logam Ni yang teremban pada zeolit alam yaitu sebesar 0,33%. Produk fraksi cair yang diperoleh dalam proses perengkahan limbah plastik LDPE yaitu sebesar 16,5% (b/b) dengan selektivitas fraksi bensin sebesar 11,26 % (b/b).

Synthesis of Ni/Natural Zeolite catalyst for hydrocracking of LDPE plastic waste fraction has been investigated. Zeolite preparation begins by immersing the zeolite to aquadest, then refluxed with 6M HCl. Furthermore, the activated zeolite was impregnated with Ni[NO3]2 using wet impregnation method, afterward it was refluxed, calcined, and reduced the Ni/ Natural Zeolite catalyst was obtained. The next stepswas characterization using XRD, SAA, AAS, FTIR, TEM, dan TG/DTA. The Ni/Natural Zeolite catalyst activity test was carried out using a semi-batch stainless steel reactor for the hydrocracking waste of LDPE plastic at a temperature of 200 oC. Hydrocracked liquid product was analyzed using GC-MS. The results showed that the amount of Ni metal that wasimpregnated on natural zeolite was 0.33%. The liquid fraction product obtained from LDPE plastic cracking process was 16.5% (w/w) with the selectivity of the gasoline fraction of 11.26% (w/w).

Kata Kunci : Nikel, zeolit alam, impregnasi basah, hidrorengkah, plastik LDPE.