PENGARUH LAMA PERENDAMAN DALAM LARUTAN MOUTHWASH BER-ALKOHOL TERHADAP COMPRESSIVE STRENGTH MICRO FIBER REINFORCED COMPOSITE

RIFQI FAHMI AFFANDI, Dr. drg. Siti Sunarintyas, M.Kes ; Prof. Dr. drg. Widjijono, S.U.

2018 | Skripsi | S1 PENDIDIKAN DOKTER GIGI

Fiber reinforced composite (FRC) adalah salah satu material restorasi gigi yang banyak digunakan karena memiliki sifat estetis dan mekanis yang baik. Fiber reinforced composite akan berinteraksi dengan makanan, minuman dan material pembersih rongga mulut. Salah satu material yang digunakan untuk membersihkan rongga mulut adalah mouthwash ber-alkohol. Tujuan penelitian ini adalah mengetahui pengaruh lama perendaman dalam larutan mouthwash ber-alkohol terhadap compressive strengh FRC. Penelitian ini menggunakanE-glass fiber reinfroced composite (everX Posterior GC, Jepang) dan mouthwash ber-alkohol (Listerine Original, Amerika Serikat). Enam belas sampel FRC dibuat silindris (diameter 4 mm dan tinggi 6 mm). Sampel dibagi menjadi empat kelompok perlakuan. Kelompok pertama direndam dalam larutan mouwthash ber-alkohol selama 0 jam, kelompok kedua 6 jam, kelompok ketiga 12 jam dan kelompok keempat 24 jam. Nilai compressive strength diukur dengan universal testing machine. Data yang diperoleh dianalisis menggunakan uji ANAVA. Hasil penelitian menunjukan nilai rerata compressive strength untuk kelompok 0 jam, 6 jam, 12 jam dan 24 jam secara berurutan adalah 293,59 SB 30,54; 285,43 SB 46,91; 268,71 SB 44,66; dan 252,19 SB 31,49 MPa. Nilai rerata compressive strength yang diperoleh menunjukan kecenderungan penurunan dari kelompok pertama hingga kelompok keempat. Hasil uji ANAVA menunjukan tidak terdapat pengaruh bermakna dari lama perendaman dalam larutan mouthwash ber-alkohol terhadap compressive strength FRC (p>0,05). Kesimpulan penelitian ini adalah lama perendaman dalam larutan mouthwash ber-alkohol menurunkan compressive strength FRC namun tidak signifikan.

Fiber reinforced composite (FRC) is one of the most widely used dental restoration materials that have good aesthetic and mechanical properties. Fiber reinforced composite will interact with food, beverages and oral cleansing materials after application asrestorations. One of the materials used to cleanse the oral cavity is an alcohol contained mouthwash. The purpose of this research is to find out the influence of thelength of immersion time in alcoholcontained mouthwash solution to compressive strength of FRC. This study used E-glass fiber reinfroced composite (everX Posterior GC, Japan) and alcohol contained mouthwash (Listerine Original, USA). Sixteen FRC samples were made in a cylindrical shape (diameter 4 mm and height 6 mm). Samples were then divided into four treatment groups. The first group was immersed in alcoholic mouwthash solution for 0 hours, second group 6 hours, third group 12 hours and fourth group 24 hours. The compressive strength value was measured by universal testing machine. The data obtained then analyzed using ANOVA test. The results showed that the mean values of compressive strength for the groups of 0 hours, 6 hours, 12 hours and 24 hours were 293.59 SD 30.54; 285.43 SD 46.91; 268.71 SD 44.66; and 252.19 SD 31.49 MPa. The average value of compressive strength obtained shows a decreasing trend from the first group to the fourth group. The result of ANOVA test showed no significant influence from soaking time in alcohol contained mouthwash solution to compressive strength of FRC (p> 0,05). The conclusion of this research is that the length of immersion time in alcohol contained mouthwash solution can decrease the compressive strength of FRC but not significant.

Kata Kunci : fiber reinforced composite (FRC), mouthwash, compressive strength