PREPARASI KATALIS Ni/BENTONIT DAN APLIKASINYA UNTUK HIDRORENGKAH MINYAK HASIL PIROLISIS PLASTIK LDPE (LOW DENSITY POLYETHYLENE)

JERRY ALDIAN PUTRA, Dr. Akhmad Syoufian; Prof. Dr.rer.nat. Karna Wijaya, M.Eng

2018 | Skripsi | S1 KIMIA

Preparasi katalis Ni/Bentonit dan aplikasinya untuk hidrorengkah minyak hasil pirolisis plastik LDPE telah dilakukan. Tujuan penelitian ini untuk preparasi katalis Ni/Bentonit, menguji efektivitas katalis, dan menentukan variasi rasio katalis. Penelitian terdiri dari tiga tahapan yaitu pirolisis, preparasi katalis Ni/Bentonit dan hidrorengkah. Tahapan pertama adalah preparasi minyak melalui proses pirolisis plastik LDPE dengan suhu 300-400 °C. Minyak hasil pirolisis dianalisis dengan GC-MS. Tahapan selanjutnya pembuatan katalis Ni/Bentonit. Preparasi katalis diawali dengan aktivasi asam pada material bentonit dengan larutan H2SO4. Pengembanan logam nikel 1% (b/b) pada material bentonit dilakukan secara impregnasi basah, dilanjutkan kalsinasi pada suhu 500 °C selama 3 jam dan reduksi dengan gas H2 20 ml/menit selama 2 jam. Katalis Ni/Bentonit dianalisis dengan FT-IR, XRD, AAS, TEM, dan SAA. Tahapan ketiga yaitu hidrorengkah minyak pirolisis dengan dan tanpa katalis. Hidrorengkah tanpa katalis dilakukan dengan variasi waktu 15 dan 30 menit. Hidrorengkah dengan katalis Ni/Bentonit dilakukan variasi rasio yaitu 0,25; 0,5 dan 1%. Proses hidrorengkah dilakukan pada suhu 300 °C dengan aliran gas H2 20 mL/menit, dan dianalisis menggunakan GC-MS. Logam nikel yang terimpregnasi dalam bentonit sebesar 0,62%. Uji efektivitas katalis Ni/Bentonit untuk menghasilkan fraksi bensin dapat dikaji dengan analisis GC-MS. Total fraksi bensin untuk pirolisis dan hidrorengkah tanpa katalis dengan waktu optimum 30 menit sebesar 75,58 dan 81,69%. Rasio katalis :umpan 0,25% menghasilkan fraksi bensin yang paling tinggi sebesar 93,48%.

The preparation of Ni/Bentonite catalyst and application for the hydrocracking from oil pyrolyzed LDPE plastics had been performed. The purpose of this study to preparation Ni/Bentonite catalyst, test the activity of catalyst, and determine the variation of the catalyst ratio. This study consisted of three steps: pyrolysis, Ni/Bentonite catalyst preparation and hydrocracking. The first step is making oil through pyrolysis process of LDPE plastic at temperature 300-400 °C and was analyzed by GC-MS. Next stage is Ni/Bentonite catalyst preparation. Preparation of catalyst was started by bentonite material acid activation using H2SO4. Ni metal 1% (w/w) then was impregnated on the material using wet impregnation method, calcination process at 500 °C for 3 hours and reduction with H2 gas 20 mL/min for 2 hours. The Ni/Bentonite catalyst was analyzed using FT-IR, XRD, AAS, TEM, and SAA. The third stage is hydrocracking with and without catalyst. Hydrocracking without catalyst conducted variation of time 15 and 30 minutes. Hydrocracking with Ni/Bentonite catalyst performed variation ratio that is 0.25; 0.5; and 1%. The hydrocracking process is carried out at 300 °C, under H2 20 mL/min at the optimum time and was analyzed by GC-MS. The percentage of nickel metal impregnated on bentonite is 0.62%. The effectiveness of Ni/bentonit catalyst for producing gasoline was determined by GC-MS analysis. Total gasoline fraction for pyrolysis and hydrocracking without catalyst with optimum time 30 minutes ie 75.58 and 81.69%. The highest gasoline fraction was 93,48%, produced by the condition of katalis:feed ratio 0,25%

Kata Kunci : hidrorengkah, katalis Ni/Bentonit, plastik, pirolisis