ANALISA KERUSAKAN BAUT WARE PLATE PADA COILER MANDREL HSM DI PT KRAKATAU STEEL

TONI PUJI RAHESTA, Lilik Dwi Setyana S.T.,M.T.

2018 | Tugas Akhir | D3 TEKNIK MESIN SV

Perkembangan industri manufaktur yang pesat mempengaruhi bidang ilmu pengetahuan dan teknologi. Salah satunya di PT Krakatau Steel di plant HSM (Hot Strip Mill) ada sebuah alat yaitu coiler mandrel yang berfungsi menggulung lembaran pelat baja. Coiler mandrel dilengkapi beberapa komponen salah satunya yaitu baut dimana komponen-komponen pada coiler mandrel apabila bekerja terus menerus komponen tidak kuat atau aus. Batas umur atau tonase maksimal coiler mandrel bekerja yaitu 90.000 ton. Setelah itu diperbaiki guna meningkatkan atau menjaga kualitas produk. Penelitian ini dilakukan pada baja karbon sedang. Pekerjaan ini termasuk melakukan proses persiapan, pembuatan spesimen uji, uji komposisi, uji kekerasan, uji kekuatan tarik, analisa struktur mikro dan uji komposisi. Hasil pengujian struktur mikro terhadap spesimen antara baut baru dan baut bekas memperlihatkan bahwa untuk fasa baja karbon sedang adalah fasa perlitic untuk semua spesimen. Hasil uji kekuatan tarik terhadap spesimen antara baut baru dan baut bekas menunjukkan bahwa nilai kekuatan tarik tidak sesuai dengan standarnya, hasil lebih tinggi atau lebih ulet. Dari hasil pengujian didapatkan nilai rata-rata yaitu 900 Mpa, sedangkan standarnya menurut DIN 8.8 800 Mpa, dan hasil uji kekerasan terhadap baut baru dan baut bekas menunjukan bahwa nilai kekerasan nya sama atau sesuai pada standarnya seperti pada tabel 2.3 yaitu nilai kekerasan 250 VHN.

The rapid development of manufacturing industry affects the field of science and technology. One of them is in PT Krakatau Steel in plant HSM (Hot Strip Mill). There is coiler mandrel that rolle sheet steel plate. Mandrel coiler is equipped with several components one of which is a bolt. The Bolt on the coiler mandrel when working continuously components are not strong or worn out. The age limit or maximum tonnage of the mandrel coiler works is 90,000 tons. After that repaired to improve or maintain product quality. The study was conducted on medium carbon steels. This work includes preparing and preparing test specimens, composition tests, hardness tests, tensile strength tests, microstructure analysis and also composition tests. The result of microstructure testing of the specimen between the new bolt and screws shows that for medium carbon steel phase. It is perlitic phase for all specimens. The result of the tensile strength test on the specimen between the new bolt and the screws indicates that the tensile strength value is not in accordance with the standard, the result is higher or more ductile. From the test results obtained an average value of 900 Mpa, while the standard as in table 2.3 is 800 Mpa, and the hardness tests results between new bolts versus old screws shows that the value of violence is similar to the standard in table 2.3. The value of violence is 250 VHN.

Kata Kunci : Kata kunci: baja karbon sedang, uji komposisi, uji kekerasan, uji tarik dan struktur mikro.