KARAKTERISTIK PELAT BETON PERKERASAN KAKU DENGAN PENAMBAHAN SELF HEALING HYDROGEL CAPSULES YANG MENGANDUNG BACILLUS CEREUS

PANGGIH TRI APRIYATI, Agus Kurniawan, ST., MT., Ph.D

2018 | Tugas Akhir | D4 TEKNIK PENGELOLAAN DAN PEMELIHARAAN INFRASTRUKTUR SIPIL

Inovasi self healing concrete telah banyak dikembangkan untuk mengatasi retak mikro pada beton. Dalam hal ini perlu diketahui pengaruh penambahan bakteri Bacillus cereus terhadap perbaikan retak beton (self healing concrete) untuk perkerasan kaku (rigid pavement) serta mengetahui perbandingan pengujian beton dengan penambahan dan tanpa penambahan bakteri Bacillus cereus. Metode yang digunakan yaitu menggunakan enkapsulasi bakteri Bacillus cereus yang diharapkan akan dapat menutup retak mikro beton. Enkapsulasi bakteri Bacillus cereus dibuat dengan mencampurkan CMC (Carboxy Meythl Celullose) dan nutrisi bakteri (Nutrient Broth), kemudan dilapisi dengan Resin Akrilik SC-1. Enkapsulasi bakteri Bacillus cereus tersebut ditambahkan kedalam campuran beton segar. Kesimpulan dari penelitian ini adalah dari hasil pengujian kuat tekan silinder beton diperoleh nilai rata-rata kuat tekan beton tanpa bakteri 21,01 MPa dan dengan penambahan bakteri 20,49 MPa. Hasilnya menunjukan bahwa tidak ada perbedaan yang signifikan antara pelat tanpa bakter dan dengan penambhan bakteri. Selain itu, Bacillus cereus dapat hidup didalam beton dan memproduksi kalsit bakteri. Secara fisik kalsit berbentuk batang dan secara kimiawi dibuktikan dengan hasil SEM-EDS yaitu dengan adanya unsur Ca, C, O serta H. Hasil dari pengujian lainnnya adalah hasil pengujian skid resistance silinder beton sebelum dilakukan dan setelah dilakukan pembebanan diperoleh hasil nilai kekesatan rata-rata permukaan perkerasan kaku ada pada nilai aman (nilai rata-rata skid resistance >55 BPN). Dari pengujian dengan sensor Accelorometer Analyzer, pelat beton (perkerasan kaku) pada percobaan 1 akan mengalami getaran atau goncangan paling besar. Sehingga perkerasan kaku akan semakin rentan mengalami kerusakan ketika terjadi getaran.

Self healing concrete innovation has been developed to overcome micro cracks in concrete. In this case, it is necessary to know the effect of the addition of Bacillus cereus bacteria to the improvement of cracked concrete for rigid pavement and to know the comparison of concrete test with the addition and without the addition of Bacillus cereus bacteria. The method used Bacillus cereus bacteria encapsulation which is expected to be able to close the cracked micro-concrete. Bacillus cereus bacterial encapsulation is made by mixing CMC (Carboxy Meythl Celullose) and bacterial nutrients (Nutrient Broth) and then coated with SC-1 Acrylic Resin. The Bacillus cereus bacteria encapsulation is added to the fresh concrete mixture. The conclusion of this research is from the concrete strength test of concrete cylinder obtained by the average value of compressive strength of concrete without bacteria 21,01 MPa and with addition of bacteria 20,49 MPa. The results showed that there was no significant difference between without bacteria in the plate and with addition of bacterial. In addition, Bacillus cereus can live in concrete and produce bacterial calcite. Physically calcite is rod-shaped and is chemically proven by SEM-EDS result that is with the element of Ca, C, O and H. The result of other test is the result of skid resistance test of concrete cylinder before it is done and after the loading is obtained the result of mean value the rigid pavement surface is at a safe value (average skid resistance value> 55 BPN). From testing with Accelorometer Analyzer, concrete plate (rigid pavement) in experiment 1 will experience the greatest vibration or shock. So that rigid pavement will be more susceptible to damage when there is vibration.

Kata Kunci : Beton Bakteri, Bakteri Bacillus cereus, Self Healing Concrete, Perkerasan Kaku.