SINTESIS DAN KARAKTERISASI Mg/Al HIDROTALSIT

MIFTAKHUL BAKHRUDDIN, Prof. Dr. Sri Juari Santosa, M.Eng; Dr. Suyanta, M.Si

2017 | Skripsi | S1 KIMIA

Telah dilakukan sintesis Mg/Al hidrotalsit dengan metode kopresipitasi menggunakan perbandingan mol Mg:Al = 2:1 dan karakterisasinya. Sintesis Mg/Al hidrotalsit dilakukan dengan titrasi menggunakan larutan NaOH 0,5 M terhadap campuran magnesium nitrat heksahidrat Mg(NO3)2.6H2O dan alumunium nitrat nonahidrat Al(NO3)3.9H2O perbandingan mol 2:1 hingga pH 10. Campuran dipanaskan pada suhu 120 ���°C selama 5 jam. Endapan disaring dan dinetralkan. Hasil sintesis dikarakterisasi menggunakan metode spektrofotometri inframerah dan difraksi sinar-X. Karakterisasi hasil sintesis menggunakan spektrofotometer inframerah menunjukkan beberapa puncak pada bilangan gelombang 3464,15 /cm menunjukkan vibrasi ulur O-H dari brucite-like layer; 1635,64 /cm menunjukkan vibrasi tekuk O-H dari air antar lapis; 1381,03 /cm menunjukkan vibrasi ulur antisimetri free NO3- antar lapis; 617,22 /cm menunjukkan vibrasi ulur logam oksida (M-O) dari Mg-O-Al. Karakterisasi hasil sintesis menggunakan difraktometer sinar-X menunjukkan beberapa puncak yang menunjukkan basal spacing d003 = 8,00 (angstrom) pada 2(theta) = 11,047���°; d006 = 3,96 (angstrom) pada 2(theta) = 22,420���°; dan d009 = 2,57 (angstrom) pada 2(theta) = 34,806���°. Hasil ini mirip dengan database JCPDS Mg/Al hidrotalsit sintesis.

The synthesis of Mg/Al hydrotalcite by coprecipitation method using Mg:Al = 2:1 mole ratio and its characterization have been carried out. Mg/Al hydrotalcite was synthesized using magnesium nitrate hexahydrate Mg(NO3)2.6H2O and aluminum nitrate nonahydrate Al(NO3)3.9H2O with mole ratio 2:1 and titrated by NaOH 0.5 M until pH 10. The mixture material was heated at 120 ���°C for 5 hours. The precipitate material was filtered and neutralized. The synthesized material was characterized using infrared spectrophotometer and X-ray diffraction. The result of characterization using infrared spectrophotometer showed several peaks at wave number 3464.15 /cm showed O-H stretching vibration of brucite-like layer; 1635.64 /cm showed O-H bending vibration of inter-layer water; 1381.03 /cm showed stretching asymetry vibration of free NO3- interlayer; 617.22 /cm represents the metal oxide stretching vibration (M-O) of Mg-O-Al. Characterization using X-ray difraction showed several peaks showing basal spacing d003 = 8.00 (angstrom) at 2(theta) = 11.047���°; d006 = 3.96 (angstrom) at 2(theta) = 22.420���°; and d009 = 2.57 (angstrom) at 2(theta) = 34.806���°. This result was similar with the JCPDS Mg/Al hidrotalsit synthesis database.

Kata Kunci : hidrotalsit, kopresipitasi