PREPARASI KOMPOSIT ARANG-Fe3O4 DARI POLIVINIL KLORIDA DENGAN METODE KARBONISASI HIDROTERMAL DAN PIROLISIS SERTA UJI ADSORPSINYA TERHADAP ION Cd(II)

SAFIRA FATWA WASKITA, Dr. Agus Kuncaka, DEA ; Prof. Dr. Mudasir, M.Eng., Ph.D

2017 | Skripsi | S1 KIMIA

Penelitian tentang preparasi komposit arang-Fe3O4 dari polivinil klorida (PVC) dan Fe3O4 untuk adsorpsi ion Cd(II) telah dilakukan. Penelitian ini bertujuan untuk mempelajari preparasi komposit arang-Fe3O4 dan mempelajari kemampuan komposit arang-Fe3O4 dalam mengadsorpsi ion logam Cd(II). Preparasi dilakukan dengan metode karbonisasi hidrotermal-pirolisis. Dalam proses karbonisasi PVC, Na2CO3 digunakan sebagai penyumbang kation penangkap Cl- yang dihasilkan dari proses deklorinasi PVC. Proses karbonisasi dilakukan dalam suasana asam (pH 6). Karakterisasi komposit arang-Fe3O4 dilakukan menggunakan FT-IR, XRD, TEM dan SAA. Hasil penelitian menunjukkan bahwa komposit arang-Fe3O4 memiliki gugus fungsi hidrofilik (O-H, C=O dan Fe-O). Komposit arang Fe3O4 memiliki luas permukaan 62,448 m2 g-1. Hasil kajian parameter kinetika adsorpsi ion Cd(II) mengikuti kinetika orde kedua semu dengan nilai konstanta laju reaksi sebesar 0,059 g mg-1 min-1. Model isoterm adsorpsi mengikuti model isoterm Freundlich dengan nilai KF sebesar 13,355 mg g-1.

A research about preparation char-Fe3O4 composite from polyvinyl chloride (PVC) and Fe3O4 for adsorption of Cd(II) ions has been conducted. This research aims to prepare char-Fe3O4 composite and examine the ability of char- Fe3O4 composite to adsorp Cd(II) ions. Preparation were done by hydrothermal carbonization-pyrolysis methods. In PVC carbonization process, Na2CO3 was used as a contributor of cation to capture Cl- which was produced from dechlorination PVC process. Carbonization process was done in acidic condition (pH 6). Char- Fe3O4 composite were characterized by FT-IR, XRD, TEM and SAA. The experimental results showed that char-Fe3O4 composite had hydrophilic functional groups (O-H, C=O and Fe-O). Char-Fe3O4 composite had surface area 62.448 m2 g-1. The adsorption kinetic parameter of Cd(II) ions followed pseudo-second order with rate constant value (k) obtained 0.059 g mg-1 min-1. The adsorption isoterm of Cd(II) ions followed Freundlich isoterm with KF value 13.355 mg g-1.

Kata Kunci : Polivinil klorida, hidrotermal, pirolisis, adsorpsi dan ion Cd(II)