PEMANFAATAN LIMBAH STYROFOAM TERSULFONASI SEBAGAI ADSORBEN UNTUK PENGHILANGAN ION LOGAM Cd(II) DI PERAIRAN

MIA AUDINA SYAHRI, Prof. Dr. Endang Tri Wahyuni, M.S. ; Dr. Roto, M.Eng.

2017 | Skripsi | S1 KIMIA

Pada penelitian ini telah dilakukan pemanfaatan limbah styrofoam yang disulfonasi sebagai adsorben untuk penghilangan ion logam Cd(II) di lingkungan. Penelitian ini terdiri dari proses sulfonasi styrofoam menggunakan larutan asam sulfat, karakterisasi, dan uji kemampuan adsorpsi styrofoam tersulfonasi terhadap ion logam Cd(II). Dalam proses sulfonasi styrofoam, telah dipelajari pengaruh konsentrasi asam sulfat dan waktu kontak. Untuk karakterisasi digunakan spektrometri FT-IR, XRD, dan SEM. Dalam adsorpsi Cd(II), parameter yang dipelajari adalah pH dan massa adsorben. Data FT-IR menunjukkan bahwa sulfonasi styrofoam telah berhasil dilakukan dengan menggunakan asam sulfat pekat dan waktu 6 jam, yang ditunjukkan dengan adanya ikatan C-S antara cincin benzena dengan gugus sulfonat. Pola difraksi menunjukkan bahwa styrofoam bersifat amorf, dan sulfonasi menyebabkan styrofoam semakin semikristalin, yang diperkuat oleh citra SEM. Adsorpsi ion Cd(II) oleh styrofoam tersulfonasi lebih baik dibandingkan dengan styrofoam, yang berlangsung maksimum pada pH 7 serta menggunakan 50 mg massa adsorben dengan hasil 9,5-9,75 mg Cd per g adsorben.

Utilization of styrofoam that has been sulfonated as adsorbent for removal Cd(II) metal ion in environment has been carried out in this research. The research starts with styrofoam sulfonation process, characterization, and adsorption ability test of the sulfonated styrofoam for metal ion Cd(II). In the styrofoam sulfonation process, effects of sulphuric acid concentration and contact time were examined. The obtained sulfonated styrofoam was characterized by FT-IR spectrometry, XRD, and SEM. In the adsorption of Cd(II), the influences pH and mass of adsorbent were evaluated. The FT-IR data show that sulfonated styrofoam has been successfully prepared by using concentrated sulphuric acid and during 6 hours, that was indicated by C-S bond between benzene ring and sulfonate group. The diffraction pattern show that styrofoam is amorphous, and sulfonation caused the styrofoam to be semicrystallin, that supported by SEM image. The adsorption of ion Cd(II) using sulfonated styrofoam is better than styrofoam, and the maximum adsorption was reached at pH 7 and using 50 mg of the adsorbent mass with result 9.5-9.75 mg Cd per g adsorbent.

Kata Kunci : adsorpsi, Cd(II), gugus sulfonat, styrofoam tersulfonasi / adsorption, Cd(II), sulfonate group, sulfonated styrofoam