PENGARUH PERLAKUAN SANDBLASTING PADA BAHAN TUMPATAN RESIN KOMPOSIT DAN SEMEN IONOMER KACA TERHADAP KEKUATAN TARIK PELEKATAN BRAKET LOGAM

ELFITRINA ARIE , drg. Christnawati, M.Kes., Sp.Ort (K) ; Prof. Dr. drg. Pinandi Sri Pudyani, SU., Sp.Ort(K)

2017 | Tesis-Spesialis | SP ORTODONSIA

Tumpatan resin komposit dan semen ionomer kaca kerapkali menyebabkan kegagalan pelekatan braket. Salah satu kriteria keberhasilan pelekatan braket yaitu persiapan permukaan pelekatan. Perlakuan sandblasting diharapkan dapat meningkatkan kekuatan pelekatan untuk menahan beban mastikasi selama perawatan ortodonti. Tujuan penelitian adalah untuk mengetahui pengaruh perlakuan sandblasting terhadap kekuatan tarik pada tumpatan bahan resin komposit dan semen ionomer kaca. Penelitian ini menggunakan diskus sejumlah 12 resin komposit dan 12 diskus semen ionomer kaca yang direndam dalam saliva buatan selama 24 jam kemudian dilakukan thermocycling secara manual. Setiap siklus thermocycling digunakan suhu 4 derajat Celsius selama 50 detik dan suhu 55 derajat Celsius selama 50 detik. Enam diskus resin komposit dan enam diskus semen ionomer kaca dilakukan sandblasting dan enam diskus resin komposit dan enam diskus semen ionomer kaca lainnya tanpa sandblasting. Braket kemudian dilekatkan pada seluruh diskus dengan adhesif resin komposit self-cured. Kekuatan tarik diuji dengan Universal Testing Machine. Hasil yang didapat (Mpa) diolah secara statistik dengan ANAVA dua jalur Hasil analisis uji ANAVA dua jalur menunjukkan tidak ada perbedaan signifikan antara sandblasting dan tanpa sandblasting (p>0,05) pada kelompok resin komposit dan semen ionomer kaca. Terdapat perbedaan signifikan kekuatan tarik antara kelompok resin komposit dan semen ionomer kaca (p<0,05). Kesimpulan penelitian adalah perlakuan sandblasting tidak mempengaruhi peningkatan kekuatan tarik pelekatan braket logam pada permukaan tumpatan resin komposit dan semen ionomer kaca. Kekuatan tarik pada permukaan tumpatan resin komposit lebih besar daripada permukaan tumpatan semen ionomer kaca.

Resin composite restoration and glass ionomer cement restoration often causing bonding failure on bracket attachment. One of the success bracket attachment criteria is preparing surface area. Surface roughening with sandblasting expected to give enough bond strength to withstand mastication forces during orthodontic treatment. The purpose of this research is to ascertain the effect of sandblasting on resin composite restoration and glass ionomer cement restoration to the tensile bond strength of metal braces. This research used 12 composite resin discs and 12 glass ionomer cement discs were immersed in artificial saliva for 24 hours and then done thermocycling process manually. Every thermocycling cycle was for 50 sec at 4 derajat Celsius and for 50 sec at 55 derajat Celsius Thermocycling cycle is done for 25 times. Six composite resin discs and 6 glass ionomer cement discs were done sandblasted. Six composite resin discs and 6 glass ionomer cement disc were done no sandblasted. All speciment group was bonding bracket using composite orthodontic adhesive self-cured. Tensile bond strength test was performed with Universal Testing Machine. The force required to tensile the bracket was recorded and the bond strength was calculated in Megapascal (MPa). Statistical analysis was performed by Two Way ANOVA. Analysis result Two Way ANOVA showed that there was no significant difference between sandblasting and without sandblasting in composite resin group and glass ionomer cement group (p>0.05). There was significant difference tensile bond strength between composite resin group and glass ionomer cement (p<0.05). The conclusion showed that there was no effect sandblasting treatment on composite resin restoration and glass ionomer cement restoration to increasing tensile bond strength of metal bracket. Tensile bond strength of composite resin restoration surface is higher than glass ionomer cement restoration surface significantly.

Kata Kunci : sandblasting, kekuatan tarik, tumpatan resin komposit, semen ionomer kaca