PENGARUH PENGGUNAAN OBAT KUMUR CHLORHEXIDINE SERTA SODIUM FLUORIDE TERHADAP KOROSIVITAS DAN DAYA LENTING KAWAT GIGI NIKEL-TITANIUM PADA ANAK USIA 12-14 TAHUN DENGAN PERAWATAN ORTHODONTIK CEKAT

TRIANITA LYDIANNA, Prof.Dr. drg. Iwa Sutardjo RS,SU.,Sp.KGA(K);Prof.Dr. drg. Al.Supartinah, SU., Sp.KGA (K)

2017 | Tesis-Spesialis | SP ILMU KESEHATAN GIGI ANAK

Pemakaian kawat nikel-titanium (NiTi) pada perawatan orthodontik rentan terhadap karies karena kebersihan mulut yang sulit dicapai, sehingga dianjurkan menggunakan obat kumur. Obat kumur chlorhexidine serta sodium fluoride (NaF) merupakan obat kumur pilihan. Tujuan penelitian ini adalah mengetahui pengaruh penggunaan obat kumur chlorhexidine serta sodium fluoride terhadap korosivitas dan daya lenting kawat NiTi pada anak usia 12-14 tahun dengan perawatan orthodonti cekat. Subjek terdiri dari 27 anak yang akan dilakukan perawatan orthodontik cekat. Subjek dibagi menjadi tiga kelompok masing-masing sembilan anak. Kelompok I tidak diberi obat kumur, kelompok II diberi chlorhexidine, dan kelompok III diberi NaF. Sebanyak 27 kawat NiTi diameter 0,012mm diukur korosinya dengan alat timbangan digital dan daya lentingnya dengan alat universal testing machine sebelum dipasang. Pagi hari setelah pemasangan, kelompok II berkumur dengan chlorhexidine dan III berkumur dengan NaF masing-masing 10 ml selama satu menit dan diulang setiap pagi selama dua minggu. Setelah dua minggu, kawat dilepas lalu diukur korosi dan daya lentingnya. Data yang diperoleh dianalisis dengan uji t tidak berpasangan. Hasil rerata korosi kelompok I (0,0021±0,00022), kelompok II (0,0023± 0,00013), uji t terdapat perbedaan bermakna (t: 2,259; p<0,05). Korosi kelompok I (0,0021±0,00022), kelompok III (0,0026±0,00016), uji t terdapat perbedaan bermakna (t: 5,402; p<0,05). Korosi kelompok II (0,0023±0,00013), kelompok III (0,0026±0,00016), uji t terdapat perbedaan bermakna (t: 4,373; p<0,05). Hasil rerata daya lenting kelompok I (0,464±0,010), kelompok II (0,477±0,009), uji t terdapat perbedaan bermakna (t: 2,848; p<0,05). Hasil rerata daya lenting kelompok I (0,464± 0,010), kelompok III (0,490±0,012), uji t terdapat perbedaan bermakna (t: 4,822, p<0,05). Hasil rerata daya lenting kelompok II (0,477±0,009), kelompok III (0,490± 0,012), uji t terdapat perbedaan bermakna (t: 2,345; p<0,05). Disimpulkan bahwa obat kumur NaF lebih meningkatkan korosi dan menurunkan daya lenting kawat NiTi dibandingkan chlorhexidine.

The use of nickel-titanium (NiTi) arch wire in orthodontic treatment was highly caries risk due to difficulty to maintain oral hygiene, and then advised to use mouthwash. Chlorhexidine and sodium fluoride (NaF) were mouthwash of choice. The aim of this study was to evaluate corrosives and resilience of NiTi arch wire after exposed to chlorhexidine and sodium fluoride in fixed-orthodontic child patients age 12-14 years old. The subjects were 27 children that would undergo fixed-orthodontic treatment. Subjects were divided into three groups consist of nine children for each. Group I was without mouthwash, group II was with chlorhexidine, and group III was with NaF. Twenty-seven 0,012 mm arch wires were scaled and resilience measured with universal testing machine before apply. Morning after applied, group II was rinsed with chlorhexidine and group III was rinsed with NaF for 10 ml during one minute every morning along two weeks. After two weeks, arch wires were taken then re-scaled and resilience re-measured. The results were analyzed by independent t-test. Mean result of corrosion for group I (0,0021±0,00022), group II (0,0023± 0,00013), t-test showed significantly different (t: 2,259; p<0,05). Corrosion for group I (0,0021±0,00022), group III (0,0026±0,00016), t-test showed significantly different (t: 5,402; p<0,05). Corrosion for group II (0,0023±0,00013), group III (0,0026± 0,00016), t-test showed significantly different (t: 4,373; p<0,05). Mean result of resilience for group I (0,464±0,010), group II (0,477±0,009), t-test showed significantly different (t: 2,848; p<0,05). Mean result of resilience for group I (0,464± 0,010), group III (0,490±0,012), t-test showed significantly different (t: 4,822, p<0,05). Mean result of resilience for group II (0,477±0,009), group III (0,490± 0,012), t-test showed significantly different (t: 2,345; p<0,05). It concluded that NaF mouthwash effected more corrosion and less resilience in NiTi arch wire than chlorhexidine.

Kata Kunci : kawat NiTi, obat kumur chlorhexidine, obat kumur sodium fluoride, korosi, daya lenting