PENGARUH DERAJAT KEASAMAN SALIVA TERHADAP KEBOCORAN TEPI RESTORASI SEMEN IONOMER KACA PADA GIGI DESIDUI ANAK - ANAK DI MADRASAH IBTIDAIYAH MUHAMMADIYAH KEDUNGWINONG

MARIA ASRI ARDIANTI, drg. Putri Kusuma Wardani Mahendra,M.Kes, Sp.KGA(K);Dr. drg. Rinaldi Budi Utomo,MS.,Sp.KGA(K)

2017 | Tesis-Spesialis | SP ILMU KESEHATAN GIGI ANAK

Di dalam rongga mulut, restorasi semen ionomer kaca selalu berkontak dengan saliva dengan derajat keasaman yang berbeda. Penelitian ini bertujuan untuk mengetahui pengaruh derajat keasaman saliva dan durasi restorasi terhadap kebocoran tepi restorasi semen ionomer kaca pada gigi desidui. Metode penelitian yang dipakai adalah penelitian eksperimental semu pada 27 siswa yang mempunyai karies di bagian labial gigi kaninus desidui rahang atas. Subyek dikelompokkan menjadi 3 kelompok berdasarkan derajat keasaman saliva, yaitu kelompok pH <5,5, pH 5,6-6,6 dan pH >6,7. Salah satu gigi direstorasi dengan semen ionomer kaca, kemudian diamati kebocoran tepi pada minggu I, minggu II, minggu III dan minggu IV setelah penumpatan. Kebocoran tepi diamati berdasarkan adanya penetrasi metilen biru disepanjang tepi restorasi. Permukaan restorasi semen ionomer kaca dibagi menjadi 4 area secara imajiner, apabila pada satu area terdapat pewarnaan tepi restorasi maka diberi skor 1. Data yang diperoleh kemudian dianalisis dengan uji statistik Chi-Square Hasil yang didapat menunjukkan bahwa kebocoran tepi restorasi semen ionomer kaca pada gigi desidui tampak pada kelompok pH <5,5. Hasil uji statistik Chi-Square menunjukkan bahwa terdapat perbedaan yang signifikan (p<0,05) kebocoran tepi restorasi semen ionomer kaca gigi desidui pada derajat keasaman saliva <5,5 minggu I dengan minggu III dan minggu IV serta antara minggu II dengan minggu IV. Berdasarkan hasil penelitian yang dilakukan di Madrasah Ibtidaiyah Muhammadiyah Kedungwinong, dapat disimpulkan bahwa kebocoran tepi restorasi semen ionomer kaca pada gigi desidui lebih besar terdapat pada subyek dengan derajat keasaman saliva <5,5. Kebocoran tepi restorasi semen ionomer kaca gigi desidui pada derajat keasaman saliva <5,5 tampak terjadi mulai minggu III.

In the oral cavity, the glass ionomer cement restoration will always contact with saliva with different degrees of acidity. This study aims to determine the effect of degrees of saliva acidity and duration of restoration on the marginal leakage of glass ionomer cement restoration in deciduous teeth. The research method used was a quasi experimental study in 27 students who had caries in the labial surface of the maxillary deciduous canine teeth. The subjects were grouped into 3 groups based on salivary acidity, ie pH <5,5, pH 5,6-6,6 and pH >6,7. One of the teeth was restored with a glass ionomer cement, then observed a marginal leakage during week I, week II, week III and week IV after restoration. Marginal leakage is observed based on the presence of methylene blue penetration along the edges of the restoration. The surface of the glass ionomer cement restoration is divided into 4 areas imaginally, if in one area there is staining the restoration edges then given a score of 1. The data obtained and analyzed by statistical test Chi-Square. The results showed that the marginal leakage of the glass ionomer cement restoration in deciduous teeth appears in the pH group of <5,5. The result of Chi-Square statistic test shows that there is a significant difference (p <0.05) marginal leakage of glass ionomer cement restoration of desidui at saliva degrees <5,5 1st week with 3rd week and 4th week and between 2nd week with 4th week after restoration. Based on the results of this study in Madrasah Ibtidaiyah Muhammadiyah Kedungwinong can be concluded that the marginal leakage of the glass ionomer cement restoration in decidual teeth is greater in subjects with salivary acidity <5.5. Marginal leakage of glass ionomer cement restoration in deciduous teeth at <5.5 salivary degree appears to occur from week III.

Kata Kunci : semen ionomer kaca, derajat keasaman saliva, kebocoran tepi