PERBANDINGAN KONSENTRASI DAN LAMA APLIKASI HYDROFLUORIC ACID TERHADAP KEKUATAN GESER LITHIUM DISILICATE GLASS CERAMIC UNTUK GIGI TIRUAN CEKAT DENGAN SEMEN RESIN SELF ADHESIVE

SRADHA PUTRA, drg. Titik Ismiyati, M.S., Sp.Pros(K), Dr. drg. Suparyono Saleh, Sp.Pros(K)

2017 | Tesis-Spesialis | SP PROSTODONSIA

Hydrofluoric acid (HF) merupakan salah satu jenis surface treatment yang digunakan untuk melekatkan gigi tiruan cekat keramik dengan semen resin. Hydrofluoric acid 5% dan 10% dapat melarutkan fase glass, lama aplikasi akan mempengaruhi reaksi pelarutan matriks kaca. Kekuatan geser yang tinggi diperlukan untuk mencegah terjadi kegagalan pelekatan pada restorasi lithium disilicate glass ceramic. Tujuan penelitian ini adalah mengkaji perbandingan konsentrasi dan lama aplikasi HF terhadap kekuatan geser lithium disilicate glass ceramic untuk gigi tiruan cekat dengan semen resin self adhesive. Penelitan ini menggunakan 24 buah sampel lithium disilicate glass ceramic berbentuk silinder (diameter 5,5 mm dengan ketebalan 3 mm) yang terbagi atas 6 kelompok (n=4). Seluruh sampel dibagi menjadi dua kelompok konsentrasi, yaitu 5% dan 10%. Setiap kelompok konsentrasi dibagi menjadi tiga kelompok lama aplikasi, yaitu 20, 60, dan 90 detik. Seluruh kelompok diuji kekuatan geser menggunakan universal testing machine. Data dianalisis menggunakan Anava dua jalur dengan tingkat kepercayaan 95% dan dilanjutkan dengan uji least significant difference (LSD). Hasil penelitian menunjukkan bahwa terdapat perbedaan bermakna pada konsentrasi dan lama aplikasi HF pada kekuatan geser (p<0,05), terdapat perbedaan tidak bermakna pada interaksi konsentrasi dan lama aplikasi HF pada kekuatan geser (p>0,05). Kesimpulan penelitian ini adalah kekuatan geser lithium disilicate dengan konsentrasi HF 10% (25,208 MPa) lebih tinggi dibandingkan dengan HF 5% (23,133 MPa). Lama aplikasi 90 detik (26,138 MPa) memiliki kekuatan geser yang lebih tinggi dibandingkan 20 detik (23,663 MPa) dan 60 detik (22,713 MPa).

Hydrofluoric acid (HF) is one of surface treatment which is needed for adhesion between ceramic brigde restoration and resin cement. Hydrofluoric acid 5% and 10% can dissolve glass phase, time application of HF has an affect on dissolution of glass matrix reactions. High shear strength is required to prevent attachment failure in lithium disilicate glass ceramic restorations. The purpose of this study is to compare concentration and time application HF on the shear strength of lithium disilicate glass ceramic for brigde restoration with self adhesive resin cement. This study used 24 samples of lithium disilicate glass ceramic cylinder (diameter 5.5 mm by thickness 3 mm) divided into 6 groups which consist of 4 samples each group. All of samples were divided into two groups on concentration i.e. 5% and 10%. Each of concentration groups were divided into three groups on time application, i.e. 20, 60 and 90 seconds. All groups were tested shear strength using universal testing machine. Data were analyzed by two-way a Anova in confident level of 95% and continued by least significant difference (LSD) test. The results showed that there was a significant difference on concentration and time of HF application on shear strength (p <0.05), no significant difference interaction in concentration and time of HF application on shear strength (p> 0.05). The conclusion of this research is shear strength of lithium disilicate with 10% HF (25.208 MPa) concentration has a higher than HF 5% (23.133 MPa). Time application 90 seconds (26.138 MPa) has a higher shear strength compared to 20 seconds (22.713 MPa) and 60 seconds (22.663 MPa).

Kata Kunci : Lithium disilicate glass ceramic, kekuatan geser, konsentrasi, lama aplikasi, hydrofluoric acid, semen resin