BEADS Ca-ALGINAT-KAOLIN SEBAGAI ADSORBEN GAS CO2

RIZA MURIANA, Dr. ADHITASARI SURATMAN, M.SI; DR. ROTO, M.ENG

2017 | Skripsi | S1 KIMIA

INTISARI Telah dilakukan penelitian tentang sintesis beads Ca-alginat-kaolin sebagai adsorben CO2. Pembuatan beads Ca-alginat-kaolin dilakukan dengan cara meneteskan larutan campuran Na-alginat dan kaolin ke larutan CaCl2 0,5 M. Variasi massa, laju alir dan waktu kontak digunakan untuk menentukan kapasitas adsorpsi. Pengujian kapasitas adsorpsi dilakukan dengan alat gas trap system secara kontinyu. Karakterisasi dilakukan menggunakan FTIR dan SEM. Pemodelan kinetika menggunakan pseudo orde pertama Lagergren dan pseudo orde kedua Ho, sedangkan pemodelan adsorpsi menggunakan isoterm Langmuir dan Freundlich. Hasil menunjukkan bahwa beads Ca-alginat-kaolin dapat digunakan sebagai adsorben gas CO2 dan memiliki kapasitas adsorpsi yang lebih besar dibandingkan dengan beads Ca-alginat. Kapasitas adsorpsi optimal yang didapatkan dengan rasio kaolin : alginat (1 : 3) pada laju alir 30 mL menit-1 dan waktu kontak 15 menit sebesar 0,1067 mmol g-1. Adsorpsi gas CO2 mengikuti model kinetika pseudo orde pertama Lagergren. Model isoterm yang sesuai untuk proses adsorpsi gas CO2 adalah model isoterm Freundlich dengan nilai KF 0,304 mmol g-1. Energi adsorpsi beads Ca-alginat- kaolin sebesar 26,681 kJ mol-1. Adsorpsi gas CO2 dengan beads Ca-alginat-kaolin merupakan fisisorpsi. Kata kunci: kaolin, beads, gas CO2, alginat, adsorpsi

ABSTRACT Ca-alginate-kaolinite beads for CO2 gas adsorbent has been studied. Ca-alginate-kaolinite was prepared by dropping Na-alginate and kaolinite into the solution of 0.5 M CaCl2. Variations of mass, flow rate and contact time were done to determine adsorption. Adsorption capacity was determined by using gas trap system continuously. Characterization of product was performed by using FTIR and SEM. The kinetic modeling was fit to pseudo first order Lagergren and pseudo second order Ho, whereas isothermal adsorption was fit to Langmuir and Freundlich. The results showed that beads of Ca-alginate-kaolinite can be used as CO2 gas adsorbent, it has a larger capacity than the Ca-alginate beads. The gas adsorption capacity was obtained byratio kaolinite : alginate (1 : 3) at a flow rate of 30 mL min-1 and 15 minutes of contact time was 0.1067 mmol g-1. Adsorption of CO2is fit tothe pseudo first order of Lagergren. The CO2 gas adsorption process in this research was the Freundlich isotherm models with the KF 0.304 mmol g-1. The adsorption energy of Ca-alginate-kaolinite beads was 26.681 kJ mol-1. The CO2 gas adsorption with Ca-alginat-kaolinite beads was found to be physisorption.

Kata Kunci : Kata kunci: kaolin, beads, gas CO2, alginat, adsorpsi