PENGARUH KELEMBABAN AKIBAT DARAH DAN SALIN TERHADAP KEBOCORAN APIKAL PADA OBTURASI SALURAN AKAR MENGGUNAKAN SILER BERBAHAN DASAR RESIN EPOKSI DAN SILER BERBAHAN DASAR MINERAL TRIOXIDE AGGREGATE

TITIK YULIAWATI, Dr. drg. Ema Mulyawati, M.S., Sp.KG (K) ; drg. Diatri Nari Ratih, M.Kes., Sp.KG., PhD

2016 | Tesis-Spesialis | SP ILMU KONSERVASI GIGI

Penutupan apikal yang baik memiliki peranan yang penting terhadap suksesnya perawatan endodontik. Kelembaban dapat mempengaruhi kualitas obturasi saluran akar yang dapat berakibat pada kebocoran apikal. Penelitian ini bertujuan untuk mengetahui pengaruh kelembaban akibat darah dan salin terhadap kebocoran apikal pada obturasi saluran akar menggunakan siler berbahan dasar resin epoksi dan siler berbahan dasar mineral trioxide aggregate (MTA). Penelitian ini menggunakan tiga puluh gigi premolar mandibula akar tunggal, dipotong pada bagian mahkota dan menyisakan panjang gigi 14 mm dari apikal dan dilakukan preparasi saluran akar dengan teknik crown down menggunakan file ProTaper rotary hingga file F3. Subjek penelitian dibagi menjadi 3 kelompok perlakuan yaitu kelompok I gigi dengan saluran akar kering, kelompok II gigi dengan saluran akar lembab akibat darah, kelompok III gigi dengan saluran akar lembab akibat salin. Masing-masing kelompok dibagi lagi menjadi 2 kelompok perlakuan yaitu kelompok A obturasi dengan siler resin epoksi, dan kelompok B obturasi dengan siler MTA. Seluruh subjek penelitian diobturasi menggunakan guta perca F3 dengan teknik single cone kemudian ditutup dengan RMGIC. Seluruh subjek penelitian diinkubasi selama 28 hari pada suhu37º, kemudian direndam dalam larutan metilen biru selama 24 jam. Seluruh subjek penelitian dipotong longitudinal sejajar aksis gigi dan diamati dibawah mikroskop stereo dengan perbesaran 20 kali dan diukur kedalaman penetrasi larutan pewarna dari apikal ke koronal. Data diolah menggunakan Anava dua jalur dan Post Hoc LSD. Hasil Anava dua jalur menunjukkan bahwa kelembaban berpengaruh terhadap kebocoran apikal pada obturasi saluran akar menggunakan siler resin epoksi maupun siler MTA. Terdapat interaksi antara kelembaban dan jenis siler terhadap kebocoran apikal. Hasil uji LSD menunjukkan bahwa terdapat perbedaan yang signifikan antar kelompok perlakuan. Kesimpulan dari penelitian ini adalah kelembaban akibat darah dan salin menyebabkan peningkatan kebocoran apikal pada obturasi saluran akar menggunakan siler berbahan dasar resin epoksi dan siler berbahan dasar MTA.

Apical sealing had an important role of the success of endodontic treatment. Moisture could influenced the quality of root canal obturation that can result in apical leakage. The aim of this study was to evaluate the effect of moisture due to blood and saline on apical leakage in the obturation using epoxy resin based sealer and mineral trioxide aggregate based sealer (MTA). In this study thirty single root mandibulary premolars were decoronated leaving a cut length 14 mm from the apical teeth and prepared with crown-down technique using ProTaper rotary files up to F3 file. Subjects were divided into 3 treatment groups. Goup I : teeth with dry root canal, Group II : teeth with moist root canal due to blood, Group III : teeth with moist root canal due to saline. Each group were divided into 2 groups. Group A : obturated with epoxy resin based sealer, Gropu B : obturated with MTA based sealer. Whole subject were obturated with gutta percha F3 using single cone technique followed by RMGIC filling. All the subject of research were incubated for 28 days in 37º, then soaked in methylene blue solution for 24 hours. The whole subject were cut parallel to the longitudinal axis and observed under a stereo microscope with 20x magnification then measured the deepest penetration of the dye solution from the apical to coronal. The data were analyzed statistically by two way analysis of variance and Post Hoc LSD test. The result of two way Anova showed that moisture affect the apical leakage in the root canal obturation using epoxy resin based sealer and MTA based sealer. There was an interaction of moisture and type of sealer to the apical leakage. The result of LSD test showed that there were significant differences between groups. From this study can be concluded that moisture due to blood and saline caused increased the apical leakage of root canal obturation using epoxy resin based sealer and MTA based sealer.

Kata Kunci : Kata kunci: obturasi, kelembaban, kebocoran apikal, siler resin epoksi, siler mineral trioxide aggregate Keyword: obturation, moisture, apical leakage, epoxy resin sealer, mineral trioxide aggregate sealer