PENGARUH ORIENTASI GLASS FIBER REINFORCED COMPOSITE TERHADAP KETAHANAN FRAKTUR TUMPATAN RESIN KOMPOSIT PACKABLE KAVITAS MESIOOKLUSODISTAL (MOD)

PITA ADINEGARA, drg.Tunjung Nugraheni, M.Kes., Sp.KG;Dr.drg. Yulita Kristanti, M.Kes., Sp.KG

2016 | Tesis-Spesialis | SP ILMU KONSERVASI GIGI

Glass fiber telah dikembangkan dalam ilmu kedokteran gigi untuk memperkuat tumpatan resin komposit di daerah posterior karena rawan terjadi fraktur akibat beban kunyah yang besar. Penelitian ini bertujuan untuk mengetahui pengaruh orientasi glass fiber reinforced composite terhadap ketahanan fraktur pada tumpatan resin komposit packable kavitas mesiooklusodistal (MOD). Penelitian ini menggunakan 24 spesimen gigi premolar maksila yang terbagi menjadi 4 kelompok. Kelompok I berisi lapisan short fiber reinforced composite dan resin komposit packable. Kelompok II berisi lapisan resin komposit flowable, unidirectional glass dan ditutup resin komposit packable. Kelompok III berisi lapisan resin komposit flowable, braided glass fiber dan ditutup dengan resin komposit packable. Kelompok IV berisi komposit packable 4 mm saja. Keempat kelompok perlakuan dilakukan thermocycling kemudian disimpan dalam inkubator selama 24 jam sebelum dilakukan uji ketahanan fraktur dengan Universal Testing Machine dengan kecepatan 1 mm/menit. Uji statistik dengan Uji Anava Satu Jalur dilanjutkan dengan Uji LSD. Nilai rerata ketahanan fraktur Kelompok I 1920,33 N, Kelompok II 1368,00 N, Kelompok III 1502,33 N, Kelompok IV 1849,67 N. Hasil analisis Uji Anava Satu Jalur menunjukkan nilai p<0,05, berarti terdapat pengaruh orientasi glass fiber reinforced composite terhadap ketahanan fraktur tumpatan resin komposit packable kavitas mesiooklusodistal. Hasil Uji LSD menunjukkan terdapat perbedaan yang signifikan antara kelompok I dengan kelompok II, antara kelompok I dan Kelompok III, terdapat perbedaan yang signifikan antara kelompok II dengan Kelompok IV, serta Kelompok III dengan kelompok IV. Tidak terdapat perbedaan yang signifikan antara kelompok II dengan kelompok III serta tidak terdapat perbedaan yang signifikan antara kelompok I dengan kelompok IV. Kesimpulan dari penelitian ini adalah ketahanan fraktur tumpatan resin komposit kavitas mesiooklusodistal (MOD) dengan orientasi random glass fiber lebih tinggi jika dibandingkan dengan unidirectional glass fiber maupun braided glass fiber.

Glass fiber has been developed in dentistry to strengthen the composite resin fillings in the posterior region as prone to fracture under the weight of large masticatory. This study aims to determine the effect of glass fiber reinforced composite orientation of fracture resistance of mesioocclusodistal cavity restored with packable composite resins. This study used 24 specimens of maxillary premolar teeth were divided into 4 groups. Group I contains a layer of short glass fiber reinforced composites and packable composite resins. Group II contains a layer of flowable composite resins, unidirectional glass fiber and covered with packable composite resins. Group III contains a layer of flowable composite resins, braided glass fiber and covered with packable composite resins. Group IV contains only 4 mm packable composite . The fourth treatment group performed thermocycling then stored in an incubator for 24 hours, afterward, they were loaded to fracture (1 mm/min) using a Universal Testing Machine. The results were statistically analyzed with One Way Anova and LSD Test. The average value of fracture resistance of Group I 1920.33 N, 1368.00 N on Group II, 1502.33 N on Group III, and 1849.67 N on Group IV. The results with One Way Anova Test that the value of p <0.05. This means that there is an influence of glass fiber reinforced composite orientation of the fracture resistance mesioocclusodistal cavity restored with packable composite resins. LSD Test results that there are significant differences between group I and group II, between group I and group III, between group II and group IV, also between group III and group IV. There are no significant differences between groups II and group III, also between group I and group IV. The conclusion of this study is the fracture resistance of mesioocclusodistal (MOD) cavity filled packable composite resins with random glass fiber is higher when compared to MOD cavity filled with unidirectional glass fiber or braided glass fiber.

Kata Kunci : orientasi, glass fiber reinforced composite, ketahanan fraktur, resin komposit packable, kavitas MOD