PEMBUATAN LAPISAN TIPIS KAWAT NANO PERAK (AgNWs) DENGAN METODE MEYER ROD

PUTRI AMALIA, Dr. Eng. Kuwat Triyana, M.Si

2016 | Skripsi | S1 FISIKA

Lapisan tipis berbasis kawat nano perak (AgNWs) telah berhasil dideposisi di atas substrat kaca menggunakan metode Meyer rod. Untuk keperluan tersebut, mula-mula dilakukan sintesis AgNWs dengan metode poliol menggunakan poly(vinyl pyrrolidone) (PVP) sebagai capping agent, etilen glokol (EG) sebagai pelarut sekaligus perduksi, dan garam CuCl2.2H2O sebagai agen pengendali. Pembuatan lapisan tipis AgNWs dilakukan menggunakan rod nomor #4 dan dipanaskan pada suhu 95 oC selama 20 menit dengan variasi konsentrasi AgNWs dalam etanol, 8 – 20 wt%. Uji morfologi lapisan tipis dilakukan menggunakan scanning electron microscopy (SEM), sementara pengukuran transmitansi dan resistasi lembar (R_s) masing-masing dilakukan menggunakan spektrofotometer UV-vis dan four point probe (FPP) yang terkopen dengan Keithley-2401. Dari hasil pengujian lapisan tipis AgNWs diperoleh bahwa kepadatan AgNWs yang terdeposisi semakin tinggi untuk konsentrasi AgNWs yang lebih tinggi. Kondisi ini mengakibatkan nilai transmitansi menurun dari 98% ke 94%, demikian pula dengan nilai resistansi lembar menurun dari 64,8 Ω/sq ke 1,4 Ω/sq.

Silver nanowires (AgNWs) based thin films have been successfully deposited on glass substrate using Meyer rod method. For that purpose, first of all AgNWs synthesized using polyol method with poly(vinyl pyrrolidone) (PVP) as a caping agent, ethylene glycol (EG) as a solvent as well as reductor, and salt CuCl2.2H2O as a control agent. Thin films AgNWs deposited using rod number #4 and heated at a temperature 95 oC for 20 minute with different concentration of AgNWs in ethanol from 8 – 20 wt%. Morphology of thin films AgNWs characterizated using scanning electron microscopy (SEM), while transmittance and sheet resistance (R_s) measured using spectophotometer UV-vis and four point probe (FPP) connected with Keithley-2401. Characterization of thin films AgNWs shows density of AgNWs deposited is higher for high concentration of AgNWs. This condition lead to decreased of transmittance from 98% to 94%, as well as decreased of sheet resistance from 64.8 Ω/sq to 1.4 Ω/sq.

Kata Kunci : deposisi, lapisan tipis, konsentrasi larutan, AgNWs, Meyer rod/deposition, thin films, solution concentration, AgNWs, Meyer rod