Comparison of Natural Beachrock and Anthropogenic Beachrock, Case Study: Okinawa-jima, Japan

LUTFIAN DARYONO, Dr. Ir. I Wayan Warmada; Ir. Anastasia Dewi Titisari, M.T., Ph.D.;Prof. Satoru Kawasaki

2016 | Tesis | S2 Teknik Geologi

Perubahan iklim serta pemanasan global merupakan masalah yang cukup serius di era ini terlebih untuk daerah pesisir pantai, Erosi, banjir rob dari air laut, perubahan garis pantai bahkan tenggelamnya sebuah daerah karena subsidence akibat erosi pantai. Meski demikian, gelombang pasang surut air laut yang cukup tinggi akan menghantam bangunan di tepi pantai dan menggerusnya perlahan hingga hancur. Maka dari itu para ilmuwan berusaha untuk membuat pondasi yang ramah lingkungan serta mampu mengurangi dampak erosi yang ditimbulkan untuk hidup yang lebih baik. Dalam penelitian berikut, investigasi lapangan serta analisis laboratorium diperlukan untuk memahami bagaimana mekanisme dan proses terbentuknya beachrock, dimana studi tersebut diambil dari Okinawa, Jepang. Setelah itu hasil yang didapatkan akan dibandingkan dengan mekanisme pembentukan beachrock buatan ditinjau dari material sementasi dan factor pembentuk batuan tersebut. Beachrock adalah batuan muda hasil dari pengendapan daerah preatik tepi pantai. Sememtasi yang membentuk batuan tersebut dikarenakan adanya proses kimiawi skala mikro yang membentuk kristal kalsium karbonat diantara partikel batuan dimana dominan semen adalah peliodal mikrit dan butiran micrite yang banyak ditemukan dalam seimantasi batu pantai. Penamaan batuan tersebut adalah biomicrite sortasi buruk (Folk, 1959), intramicrite sortasi buruk (Folk, 1959), bioclast grainstone (Dunham, 1962), intraclast grainstone (Dunham, 1962), and lithoclast grainstone (Dunham, 1962). Sedangkan untuk batu buatan sintetis, pemanfataan microbacteria sebagai reagen penyemenan antar partikel, spesies yang digunakan adalah Pararodhobacter sp dan Oceanic Spherea sp., kemudian pH serta konsentrasi ion kalsium akan diukur sebagai nuttisi banteri yang digunakan. Setelah hasil didapatkan selama 2 minggu percobaan, barulah hasil penyemenan dapat dibandingkan dengan batuan asli yang terbentuk di alam. Pembanding salah satunya dalah berdasarkan uji kuat tekan pada batuan asli dan buatan, dimana didapatkan hasil antara 4 MPa hingga 8 MPa. Kata kunci: beachrock, kalsium karbonat, anthropogenik, microorganism.

Climate change and global warming produce serious problems along coastal area one of which is erosion. The impact of the flooding of coastal cities by saltwater, the annual shifting of shoreline, and the submerging of some islands due to the erosion. Nevertheless, as the wave approaches the coastline it loses its energy as the result of the increasing friction against the seabed. Erosion that hit by the time will have damage impact for development construction near/on the sea, such as high way, bridge concrete, and also airport building. Nowadays, researcher tried to make eco-friendly concrete and synthetic beachrock using microorganism reagent. Anthropogenic beachrock aims and purposes for reduce erosional degree and protected important buildings for better environment development. In this study, field investigations and laboratory analysis are performed, both of which are aimed at understanding the formation mechanism of fresh beachrock in Okinawa Prefecture, Japan. Afterwards, the difference of solidification mechanism between artificial beachrock and the natural can be comprehended, upon the assumption that the cement type and other additional materials determines the strength of the material. Beachrock is recent sedimentary rock in the phreatic (upper neritic) vadose environment. Cementations that develop in vadose zone vary because the chemical microenvironments in the pores change frequently through time, key factors of carbonat precipitated was peloidal micrite and micritic grains enrichment that found in shore line deposits sedimentary. Name of the characteristics beachrock as poorly washed biomicrite (Folk, 1959), poorly washed intramicrite (Folk, 1959), bioclast grainstone (Dunham, 1962), intraclast grainstone (Dunham, 1962), and lithoclast grainstone (Dunham, 1962). Microbes that we used is Pararodhobacter sp. and Oceanic Spherea sp., then measuring pH and also calcium ion consumption that we add daily for nutrient of bacteria. Solidification test inside laboratory scale to forming beachrock in syringe volume were powerful enough to compared with natural beachrock in wild life, for example based on strength parameter. The average UCS strength is between 4 MPa and 8 MPa, quite similar with natural beachrock UCS strength.

Kata Kunci : beachrock, calcium carbonate, anthropogenic, microorganism.