SINTESIS, KARAKTERISASI DAN UJI AKTIVITAS KATALIS Cr/BENTONIT PADA REAKSI HIDRORENGKAH CPO PARIT MENJADI BIOGASOLIN

ERWIKA DHORA JATI, Dr. Akhmad Syoufian ; Prof. Dr. Karna Wijaya, M.Eng

2016 | Skripsi | S1 KIMIA

Telah dilakukan penelitian tentang pembuatan biogasolin dari CPO parit melalui proses hidrorengkah dengan katalis Cr/bentonit. Bentonit diaktivasi menggunakan asam sulfat 1 M sehingga diperoleh sampel bentonit teraktivasi asam (H-bentonit). Preparasi katalis dilakukan dengan metode impregnasi larutan garam prekusor Cr(NO3)·9H2O pada bentonit teraktivasi asam. Karakterisasi katalis meliputi analisis FTIR, XRD, XRF, BET, TEM dan uji keasaman dengan adsorpsi basa amonia, sedangkan hasil uji aktivitas katalis dianalisis menggunakan GC-MS. Hasil penelitian menunjukkan bahwa proses impregnasi pada sintesis bentonit menyebabkan perubahan pada karakter fisiokimiawi katalis. Proses impregnasi mengakibatkan peningkatan luas permukaan bentonit, rerata jari-jari pori, volume pori total dan keasaman katalis secara berturut-turut yaitu 60,239 m2/g, 117,918 A, 17,76 cc/g dan 8, 789 mmol/g. Hasil uji aktivitas dan selektivitas katalis diperoleh dari variasi katalis H-bentonit dan Cr/bentonit dengan konversi biogasolin dari proses hidrorengkah 50 mL CPO parit secara berturut-turut sebesar 8,12% dan 9,64%. Uji selektivitas katalis dianalisis dengan GC-MS menghasilkan produk dominan fraksi biogasolin sebesar 61,19% dengan Cr/bentonit dan 48,27% fraksi gasolin dengan H-bentonit.

The synthesis of Cr/bentonite catalyst for the hydrocracking of pond CPO to biogasoline has been conducted. Bentonite has been activated by sulphuric acid of 1 M to obtain acid activated bentonite (H-bentonite). Preparation of catalyst was done by impregnating salt precursor solution Cr(NO3)·9H2O on acid activated bentonite. Catalyst characterization were analyzed using FTIR, XRD, XRF, BET, TEM and acidity test through ammonia base adsorption and catalyst activity test result was analyzed by GC-MS. The results showed that impregnated Cr on bentonite caused a change of physiochemistry character of bentonite. Impreganation process increased specific surface area, pore size average, total pore volume and catalyst acidity of 60.239 m2/g, 117.918 A, 17.76 cc/g, 8.789 mmol/g respectively. The result showed that conversion of 50 mL pond CPO into biogasoline were 8.12% and 9.64% using H-bentonite and Cr/bentonite respectively. On using Cr/bentonite, the product was dominated by gasoline (61.19%), meanwhile with H-bentonite obtained 48.27% of gasoline.

Kata Kunci : Hidrorengkah, CPO parit, Cr/bentonit, biogasolin