Kinetika Lepas Lambat Ion Fe(III) dan NH4+ dari Komposit Alginat/Zeolit-Fe(III)-NH4+

HASTI UNGGUL PAMBUDI , Dr. Dwi Siswanta, M.Eng; Dr. Yateman Arryanto

2016 | Skripsi | S1 KIMIA

Telah dilakukan sintesis komposit alginat/zeolit-Fe(III)-NH4+ (A/Z-Fe(III)-NH4+) pada variasi konsentrasi NH4+. Tujuan penelitian ini adalah mensintesis komposit A/Z-Fe(III)-NH4+ yang dapat melepaskan Fe(III) dan NH4+ secara lambat dan mempelajari kinetika lepas lambat Fe(III) dan NH4+ dari komposit A/Z-Fe(III)-NH4+. Komposit yang diperoleh dikarakterisasi dengan menggunakan spektrofotometer inframerah dan difraktometer sinar X. Penentuan Fe(III) total dilakukan dengan menggunakan metode destruksi basah, sedangkan kandungan N total dengan metode Kjeldahl. Uji pelepasan Fe(III) dan NH4+ dari komposit A/Z-Fe(III)-NH4+ dilakukan dalam media asam sitrat. Komponen Fe(III) yang terlepas dari komposit dianalisis menggunakan spektrofotometer serapan atom (SSA), sedangkan komponen NH4+ yang terlepas dianalisis menggunakan spektrofotometer UV-Vis. Hasil karakterisasi dengan spektrofotometer inframerah menunjukkan bahwa spektra pada komposit A/Z-Fe(III)-NH4+ merupakan gabungan dari spektra gugus fungsi alginat dan zeolit. Difraktogram sinar-X komposit menunjukkan bahwa komposit A/Z-Fe(III)-NH4+ mempunyai sifat semikristalin. Kenaikan konsentrasi NH4+ dapat menurunkan penyerapan Fe(III) di dalam komposit. Kinetika lepas lambat Fe(III) dan NH4+ dari komposit mengikuti model Korsmeyer-Peppas. Laju pelepasan Fe(III) lebih lambat daripada laju pelepasan NH4+ yang dibuktikan dengan nilai k Fe(III) (0,318 hingga 0,380 jam-1) yang lebih kecil daripada nilai k NH4+ (0,570 hingga 0,702 jam-1).

Synthesis of alginate/zeolite-Fe(III)-NH4+ (A/Z-Fe(III)-NH4+) composite in various NH4+ concentration has been done. The aims of this research were to synthesize A/Z-Fe(III)-NH4+ composite which could release Fe(III) and NH4+ slowly and studied Fe(III) and NH4+ ions release from A/Z-Fe(III)-NH4+ composite. The obtained composites were characterized using infrared spectrophotometer and X-ray diffractometer. The Fe(III) total content in composite was determined by wet destruction and total N content by Khedjdhal method. The release of Fe(III) and NH4+ from A/Z-Fe(III)-NH4+ were studied in citric acid medium. The release of Fe(III) from composite was analysed by using atomic absorption spectrophotometer (AAS) while analysis of released NH4+ was carried out by using UV-Vis spectrophotometer. The infrared spectra of composite showed that spectra from A/Z-Fe(III)-NH4+ composite was combination from spectra functional group of alginate and zeolite. X-ray diffractions showed that composite had semi-crystalline characteristic. The increase in the concentration of NH4+ may decrease the absorption of Fe(III) in the composite. Slow release kinetics of Fe(III) and NH4+ from composite followed Korsmeyer-Peppas model. Release rate Fe(III) was slower than NH4+, was proved by the value of k from Fe (0.318 to 0.380 hour-1) smaller than k value of NH4+ (0.570 to 0.702 hour-1).

Kata Kunci : komposit, alginat/zeolit-Fe(III)-NH4+, asam sitrat, lepas lambat/composite, alginate/zeolite-Fe(III)-NH4+, citric acid, slow release