MATERIAL Ag2O/BENTONIT SEBAGAI ANTIBAKTERI Escherichia coli

ILYAS TAUFIK ABDUL AZIZ , Drs. Iqmal Tahir, M.Si. ;Prof. Dr.rer.nat. Karna Wijaya, M.Eng.

2016 | Skripsi | S1 KIMIA

Sintesis, karakterisasi dan uji aktivitas antibakteri material Ag2O/bentonit terhadap bakteri Escherichia coli telah dilakukan. Tujuan penelitian ini adalah dapat membuat material Ag2O/bentonit yang memiliki sifat antibakteri, dan dapat menentukan konsentrasi Ag2O/bentonit yang memberikan aksi antibakteri paling efektif terhadap E. coli. Preparasi diawali dengan perlakuan terhadap bentonit yang dihaluskan dan disaring 100 mesh, kemudian diaktivasi dengan H2SO4 1 M untuk menghasilkan H/bentonit. Sintesis Ag2O/bentonit dilakukan dengan cara impregnasi basah. Produk dikarakterisasi dengan FTIR, XRD dan SEM-EDS. Aktivitas antibakteri produk diuji dengan metode Agar Diffusion Test dengan variasi konsentrasi 5, 10, 15 dan 20 mg/L. Hasil penelitian menunjukkan jika Ag2O/bentonit telah berhasil terbentuk yang dikonfirmasi oleh difraktogram XRD dengan keberadaan puncak pada 2θ = 33,92 dan 37,67o. Tampilan SEM menunjukkan jika modifikasi bentonit menjadi Ag2O/bentonit menyebabkan perubahan pada permukaan bentonit. Data EDS menunjukkan kandungan Ag di dalam bentonit meningkat 20,32% (b/b) setelah dimodifikasi menjadi Ag2O/bentonit. Hasil uji antibakteri menunjukkan bahwa ketiga produk memiliki aktivitas antibakteri. Ag2O/bentonit dengan konsentrasi 20 mg/L menunjukkan aktivitas antibakteri paling efektif .

Synthesis, characterization and antibacterial activity test of Ag2O/bentonite against Escherichia coli bacteria had been done. The aim of this experiment were to make Ag2O/bentonite material that has antibacterial properties, and determine the concentration of Ag2O/bentonite which provided the most effective antibacterial action against E. coli. Preparation initiated with the treatment of bentonite that was crushed and sieved to 100 mesh, then it was activated with H2SO4 1 M to produce H/bentonite. Synthesis of Ag2O/bentonite was done by wet impregnation. Products were characterized by FTIR, XRD and SEM-EDS. Antibacterial activity of the products were tested with Agar Diffusion Test method with concentrations variation of 5, 10, 15 and 20 mg/L. The results of experiment showed that Ag2O/bentonite had been formed. The formation of Ag2O/bentonite was confirmed by XRD difractogram with appearance of peaks at 2θ = 33.92 and 37.67o. SEM image showed that bentonite modification to Ag2O/bentonite changed surface of bentonite. EDS data showed Ag wt % in the bentonite increased 20.32 wt % after modified to Ag2O/bentonite. The result of antibacterial test showed that all three products had antibacterial activity. The Ag2O/bentonite with concentration 20 mg/L showed the most effective antibacterial activity.

Kata Kunci : Keyword: Ag2O/bentonite, antibacteria, bentonite, Eschericia coli