STUDI HUBUNGAN ANTARA KOMPOSISI Mn DAN Zn TERHADAP TETAPAN SUSEPTIBILITAS PADA NANOPARTIKEL MAGNETIK MANGANESE ZINC FERRITE (Mn(1-x)Zn(x)Fe2O4)

TEPPEI JORDY L T, Dr. Edi Suharyadi, M.Eng

2016 | Skripsi | S1 FISIKA

Telah dilakukan pengukuran tetapan suseptibilitas terhadap nanopartikel magnetik manganese zinc ferrite (Mn(1-x)Zn(x)Fe2O4) dalam bentuk serbuk dengan variasi nilai x, dengan x = 0,4, 0,5, 0,6, 0,7, 0,8. Penelitian dilakukan dengan metode Gouy, dan menghasilkan nilai tetapan suseptibilitas berturut-turut (6,37 ± 0,39) x 10-5 m^3 per kg; (4,74 ± 0,81) x 10-5 m^3 per kg; (1,01 ± 0,02) x 10-5 m^3 per kg; (3,31 ± 0,23) x 10-6 m^3 per kg; (1,10 ± 0,04) x 10-6 m^3 per kg dengan ukuran partikel (20,53 ± 0,18) nm; (21,06 ± 0,32) nm; (35,03 ± 0,66) nm; (12,68 ± 0,14) nm; (13,37 ± 0,42) nm dan parameter kisinya (8,56 ± 0,02) Angstrom ; (8,56 ± 0,03) Angstrom ; (8,59 ± 0,07) Angstrom ; (8,55 ± 0,04) Angstrom ; (8,56 ± 0,07) Angstrom. Semakin besar nilai x maka tetapan suseptibilitasnya semakin kecil. Tetapan suseptibilitas dipengaruhi oleh ukuran butir dimana nilai suseptibilitasnya meningkat seiring dengan mengecilnya ukuran partikel dan tidak dipengaruhi oleh parameter kisinya

A study about susceptibility measurement of nanoparticles magnetic manganese zinc ferrite (Mn(1-x)Zn(x)Fe2O4) in powder form with x = 0.4, 0.5, 0.6, 0.7, 0.8 has been conducted. The research was done using Guoy method, and the resulting susceptibility constant values are as followes (6.37 ± 0.39) x 10-5 m^3 per kg; (4.74 ± 0.81) x 10-5 m^3 per kg; (1.01 ± 0.02) x 10-5 m^3 per kg; (3.31 ± 0.23) x 10-6 m^3 per kg; (1.10 ± 0.04) x 10-6 m^3 per kg with particle size are (20.53 ± 0.18) nm; (21.06 ± 0.32) nm; (35.03 ± 0.66) nm; (12.68 ± 0.14) nm; (13.37 ± 0.42) nm dan lattice parameter are (8.56 ± 0.02) angstrom ; (8.56 ± 0.03) angstrom ; (8.59 ± 0.07) angstrom ; (8.55 ± 0.04) angstrom ; (8.56 ± 0.07)angstrom. The value of x increase with decreasing of susceptibility constant. Susceptibility constant influenced by particles size, where susceptibility constant is increasing along with decreasing of particles size and not affected by lattice parameter.

Kata Kunci : nanopartikel, kopresipitasi, suseptibilitas magnetik, manganese zinc ferrite (Mn(1-x)Zn(x)Fe2O4).