Laporkan Masalah

DESULFURISASI OKSIDATIF DIBENZOTIOFENA MENGGUNAKAN KATALIS MoOX TERIMPREGNASI PADA PASIR SILIKA MAGNETIK DARI PANTAI PARANGTRITIS

FIDELA DINI R, Prof. Dra. Wega Trisunaryanti, M.Si., Ph.D., Eng. ; Prof. Dr. Triyono, S.U.

2022 | Skripsi | S1 KIMIA

Penelitian desulfurisasi oksidatif dibenzotiofena (DSO-DBT) menggunakan katalis MoOx terimpregnasi pada pasir silika magnetik dari pantai Parangtritis (MoOx-PP) telah dilakukan. Penelitian dilakukan dengan tujuan mempelajari karakter pasir silika magnetik dari Parangtritis (PP) dan katalis MoOx-PP, serta aktivitas katalis pada reaksi DSO-DBT dengan variasi temperatur dan waktu reaksi, serta volume H2O2. Preparasi katalis MoOx-PP dilakukan dengan menggunakan metode impregnasi basah. Katalis MoOx-PP dikarakterisasi menggunakan XRD, SEM-EDX, SAA, FTIR, dan TEM dan diuji keasamannya dengan metode adsorpsi uap basa NH3 secara gravimetri. Variasi yang dilakukan terdiri dari temperatur reaksi 30, 40, 50, dan 60 derajat celsius. Waktu reaksi divariasi 10, 20, 30, dan 40 menit. Variasi volume H2O2 sebesar 0,21; 0,42; dan 0,63 mL. Produk DSO-DBT dikarakterisasi dengan spektrofotometer UV-Vis. Katalis PP dan MoOx-PP memiliki total keasaman sebesar 1,48 dan 3,07 mmol/g. Kedua katalis memiliki sifat magnet yang ditunjukkan dengan dapat ditarik magnet. Katalis MoOx-PP menunjukkan pola difraktogram dengan puncak SiO2, MoO3, dan Fe3O4. Katalis MoOx-PP memiliki morfologi berbentuk bulatan atau bola dengan permukaan yang kasar, ukuran tidak beraturan, dan terbentuk aglomerasi. Luas permukaannya adalah 4,506 m2/g dengan volume pori 0,034 cm3/g, dan diameter pori 30,044 nm yang termasuk ke dalam material mesopori. Aktivitas katalis MoOx-PP dari reaksi DSO-DBT (83,35 %) optimum pada variasi temperatur dan waktu reaksi 40 derajat celsius dan 30 menit, dan volume H2O2 0,42 mL. Aktivitas katalis PP pada reaksi DSO-DBT sebesar 77,20 % pada temperatur dan waktu reaksi 40 derajat celcius dan 30 menit, dan volume H2O2 0,42 mL.

Research on oxidative desulfurization of dibenzothiophene (DSO-DBT) using MoOx catalyst impregnated on magnetized silica sand from Parangtritis beach (MoOx-PP) has been carried out. The research was conducted with the aim of studying the character of the magnetic silica sand from Parangtritis (PP) and MoOx-PP catalyst and the catalyst activity on ODS-DBT reaction under variations of temperature and time reaction as well as volume of H2O2. The preparation of MoOx-PP catalyst was conducted using wet impregnation method. The MoOx-PP catalyst was characterized using XRD, SEM-EDX, SAA, FTIR, and TEM and gravimetrically tested for acidity using NH3 base vapor adsorption. The variations of reaction times was 10, 20, 30, and 40 min. The reaction temperature was varied from 30, 40, 50, to 60 celcius degree. The volume of H2O2 was conducted in a variation of 0.21; 0.42; and 0.63 mL. The result of ODS-DBT reaction was characterized by UV-Vis spectrophotometer. The results showed that the P and MoOx-PP catalysts have a total acidity of 1,48 and 3.07 mmol/g. The P and MoOx-PP catalyst had magnetic properties as evidenced by being attracted to a magnet. The diffractogram pattern showed the peaks of SiO2, MoO3, and Fe3O4 on MoOx-PP catalyst. The MoOx-PP catalyst has a spherical morphology with a rough surface, irregular size, and agglomeration forms with surface area of 4.506 m2/g, pore volume of 0.034 cm3/g, and average pore diameter of 30.044 nm. The optimum catalyst activity of MoOx-PP on ODS-DBT reaction (83.35 wt%) resulted in a temperature of 40 celcius degree, time of 30 min, and H2O2 volume of 0.42 mL. The activity of P catalyst on ODS-DBT reaction was 77.20 wt% on a temperature of 40 celcius degree, time of 30 min, and H2O2 volume of 0.42 mL.

Kata Kunci : desulfurisasi oksidatif, dibenzotiofena, MoOx, pasir pantai Parangtritis.

  1. S1-2022-424219-abstract.pdf  
  2. S1-2022-424219-bibliography.pdf  
  3. S1-2022-424219-tableofcontent.pdf  
  4. S1-2022-424219-title.pdf