SINTESIS Ni-Zn LAYERED HYDROXIDE SALTS (Ni-Zn LHS) TERIMOBILISASI ASAM GALAT SEBAGAI ADSORBEN REDUKTIF [AuCl4]¯ DAN PUNGUT ULANG EMAS HASIL REDUKSINYA MENGGUNAKAN NATRIUM SITRAT

Sigit Fitriyanto, Prof. Drs. Sri Juari Santosa, M.Eng., Ph.D.; Prof. Indriana Kartini, S.Si., M.Si., Ph.D.

2022 | Skripsi | S1 KIMIA

Sintesis Ni-Zn Layered Hydroxide Salts (Ni-Zn LHS) terimobilisasi asam galat sebagai adsorben reduktif [AuCl4]¯ dan pungut ulang emas hasil reduksinya menggunakan natrium sitrat telah dilakukan. Material Ni-Zn LHS disintesis menggunakan metode grinding dengan mencampurkan Ni(NO3)2.6H2O dan Zn(NO3)2.4H2O dengan perbandingan mol 2:1. Campuran tersebut ditambahkan padatan NaOH dengan variasi mol reaktan OH:total Ni-Zn yakni 0,3; 0,6; dan 0,9. Imobilisasi asam galat dilakukan pada material Ni-Zn LHS untuk selanjutnya digunakan pada proses adsorpsi dan reduksi [AuCl4]¯ menjadi Au(0). Natrium sitrat digunakan sebagai agen pengkaping dalam proses desorpsi Au(0) dan menghasilkan nanopartikel emas (AuNP). AuNP hasil desorpsi Au(0) dari Ni-Zn LHS AG optimum pada pH 7, dengan konsentrasi natrium sitrat 20 mM, dan waktu sonikasi 3 jam. Puncak serapan karakteristik AuNP hasil sintesis teramati pada panjang gelombang 514 - 517 nm. AuNP hasil sintesis tidak stabil setelah 2 bulan dengan ukuran 5-50 nm.

Synthesis of gallic acid immobilized Ni-Zn Layered Hydroxide Salts (Ni-Zn LHS) for reductive adsorption of [AuCl4]¯ and recovery of the reduced gold using sodium citrate have been studied. Ni-Zn LHS was synthesized by grinding methods, mixing Ni(NO3)2.6H2O and Zn(NO3)2.4H2O at mole ratio of 2:1. The Mixture was added with solid NaOH at mol ratio of OH:Ni-Zn total was equal to 0.3, 0.6, and 0.9. Gallic acid immobilization was carried out on Ni-Zn LHS material for further use in the adsorption and reduction of [AuCl4]¯ to Au (0). Sodium citrate was used as a capping agent during the desorption process of Au (0) and produced gold nanoparticles (AuNP). AuNP as the desorption of Au (0) from Ni-Zn LHS AG was optimum at pH 7, with sodium citrate concentration 20 mM, and sonication time 3 hours. The characteristic absorption peak of the synthesized AuNP was observed at wavelength 514-517 nm. The synthesized AuNP was unstable to survive for 2 months after synthesis with size of 5-50 nm.

Kata Kunci : Kata kunci: asam galat, grinding, Ni-Zn LHS, nanopartikel emas, natrium sitrat