PREPARASI DAN KARAKTERISASI TiO2 TERMODIFIKASI CAMPURAN OKSIDA SnO2 DAN La2O3 UNTUK MENINGKATKAN AKTIVITAS FOTODEGRADASI METILEN BIRU DI BAWAH SINAR TAMPAK

FUADATUS SHOLIHAH, Taufik Abdillah Natsir, S.Si., M.Sc., Ph.D; Prof. Dr. Endang Tri Wahyuni, M.S.

2022 | Skripsi | S1 KIMIA

Preparasi TiO2 termodifikasi campuran oksida SnO2 dan La2O3 telah dilakukan untuk menghasilkan fotokatalis yang aktif pada sinar tampak. Preparasi dilakukan dengan metode ko-presipitasi yang meliputi proses pelarutan reaktan menggunakan larutan HNO3 dan pengendapan kembali menggunakan larutan NaOH. Padatan yang diperoleh dikalsinasi dan dikarakterisasi menggunakan instrumentasi XRD, SRUV, FTIR, dan SEM-EDX. Rasio Sn/La yang optimal ditentukan melalui uji fotodegradasi metilen biru pada sinar tampak. Mekanisme fotodegradasi diketahui melalui uji penangkap radikal dengan menambahkan 2-propanol, benzoquinon, dan EDTA ke dalam sampel metilen biru. Hasil karakterisasi m enunjukkan bahwa material hasil preparasi terdiri dari campuran oksida SnO2/La2O3/TiO2 yang memiliki energi celah pita lebih rendah sehingga aktivasi fotokatalis dapat terjadi di bawah sinar tampak. Variasi komposisi optimal diperoleh pada rasio Sn/La 10 yang menghasilkan penurunan konsentrasi metilen biru mencapai 81,3%. Peningkatan aktivitas fotokatalitik pada SnO2/La2O3/TiO2 berasal dari kombinasi penurunan energi celah pita, peningkatan adsorpsi , serta penghambatan proses rekombinasi. Hasil uji penangkap radikal menunjukkan bahwa aktivitas fotokatalitik SnO2/La2O3/TiO2 paling banyak dipengaruhi oleh pembentukan spesies radikal hidroksil.

The preparation of TiO2 modified by SnO2 and La2O3 mixed oxides had been carried out to produce photocatalysts that can be activated under visible light. The preparation was carried out by the co-precipitation method which included the dissolution of the reactants using HNO3 solution and re-precipitation using NaOH solution. The solids obtained were calcined and characterized using XRD, SRUV, FTIR, and SEM-EDX instrumentations. The optimal Sn/La ratio was determined by the photodegradation test of methylene blue under visible light. The mechanism of photodegradation was determined through a radical scavenging test by adding 2-propanol, benzoquinone, and EDTA to the methylene blue sample. The characterization results showed that the prepared material consisted of SnO2/La2O3/TiO2 mixed oxides which had a lower band gap energy so that photocatalyst activation can occur under visible light. The optimal composition variation was obtained at the ratio of Sn/La 10 which resulted in a decrease in the concentration of methylene blue up to 81.3%. The increase in photocatalytic activity in SnO2/La2O3/TiO2 came from a combination of decreasing band gap energy, increasing adsorption, and inhibiting the recombination process. The results of the radical scavenging test showed that the photocatalytic activity of SnO2/La2O3/TiO2 was most influenced by the formation of hydroxyl radical species.

Kata Kunci : ko-presipitasi, kombinasi semikonduktor, metilen biru, TiO2