FOTODEGRADASI ZAT WARNA KONGO MERAH DI BAWAH PAPARAN SINAR TAMPAK DENGAN ADANYA FOTOKATALIS TiO2 TERDOPING SULFAT

NYAYU SHAFIYAH MAHIRA, Prof. Dr. Endang Tri Wahyuni, M.S.;Taufik Abdillah Natsir, M.Sc., Ph.D

2021 | Skripsi | S1 KIMIA

Pada penelitian ini dilakukan uji aktivitas TiO2 terdoping sulfat di bawah paparan sinar tampak untuk mendegradasi kongo merah. Proses doping sulfat pada TiO2 dilakukan melalui metode hidrotermal menggunakan autoclave. Preparasi dilakukan menggunakan H2SO4 sebagai sumber dopan sehingga dihasilkan TiO2 terdoping sulfat dengan berbagai variasi konsentrasi. Karakterisasi TiO2 terdoping sulfat dilakukan dengan instrumen FTIR, XRD, SRUV dan SEM-EDX. Aktivitas fotokatalik TiO2 dan TiO2 terdoping sulfat diuji dalam proses degradasi kongo merah. Proses optimasi waktu penyinaran, massa fotokatalis, dan pH larutan dilakukan pada paparan sinar tampak. Larutan yang telah didegradasi dianalisis absorbansinya dengan spektrofotometer UV-Vis. Hasil penelitian menunjukkan bahwa adanya dopan sulfat pada TiO2 dapat menurunkan energi celah pita. Energi celah pita terendah didapatkan oleh TiO2 terdoping sulfat dengan kadar terdoping 10% yaitu sebesar 2,92 eV dan dapat mendegradasi kongo merah secara lebih efektif dibandingkan dengan TiO2 di bawah paparan sinar tampak. Fotodegradasi zat warna kongo merah dengan adanya fotokatalis TiO2 terdoping sulfat terbaik tercapai dengan kondisi waktu penyinaran 90 menit, massa fotokatalis 30 mg, dan pH 4 yaitu sebesar 97,87%.

Sulfate doped TiO2 activity under visible light irradiation was measured for congo red degradation. Doping sulfate into TiO2 lattice process was carried out by hydrothermal method with autoclave. Sulfuric acid (H2SO4) was used as doping source and various sulfate doped TiO2 concentrations were prepared. The as-prepared sulfate doped TiO2 obtained was characterized by FTIR, XRD, SRUV and SEM-EDX instruments. The photocatalytic activity of TiO2 and sulfate doped TiO2 was evaluated for congo red degradation. Irradation time, photocatalyst dosage, and solution's pH were optimazed under visible light irradiation. The degradation yield was analyzed using UV-Vis spectrophotometer. The research showed that the sulfate doped in TiO2 lattice could decrease the band gap energy of the obtained material. The best band gap of the photocatalysts was 2,92 eV and was given by sulfate doped TiO2 10%. The highest performance of photocatalyst in the degradation of congo red under visible light irradiation was 97,87% where the amount of catalyst was 30 mg, the pH solution was 4, and the reaction time was 90 minutes.

Kata Kunci : doping sulfat, fotodegradasi, kongo merah, sinar tampak, TiO2