Laporkan Masalah

SINTESIS 2-(2-FURILMETILIDEN)SIKLOPENTANON DAN 2,5-BIS(2-FURILMETILIDEN)SIKLOPENTANON DENGAN MENGGUNAKAN La2O3 SEBAGAI KATALIS

KURNIA SUCI, Taufik Abdillah N., M.Sc. Ph.D; Drs. Roto, M.Eng, Ph.D

2021 | Skripsi | S1 KIMIA

Sintesis 2-(2-furilmetiliden)siklopentanon (FCP) dan 2,5-bis(2-furilmetiliden)siklopentanon (F2CP) melalui reaksi kondensasi aldol telah berhasil dilakukan menggunakan katalis La2O3 yang telah dipreparasi. Penelitian ini bertujuan untuk melakukan preparasi katalis La2O3 melalui metode presipitasi , menganalisis stabilitas La2O3 sebagai katalis reaksi kondensasi aldol, melakukan sintesis senyawa FCP dan F2CP serta menentukan kondisi optimum reaksi kondensasi aldol yang terkatalisis La2O3. La2O3 merupakan katalis heterogen yang bersifat basa kuat sehingga berpotensi untuk menggantikan katalis homogen yang banyak digunakan pada reaksi kondensasi aldol sebelumnya. Pada tahap preparasi La2O3 secara presipitasi, La2O3 dilarutkan dalam HNO3 dan akuades dan ditambahkan NaOH hingga mencapai pH 12. Padatan yang terbentuk disaring dan dicuci hingga mencapai pH netral. Padatan La2O3 dikeringkan dan dikalsinasi pada suhu 650 derajat Celsius selama 3 jam. Katalis yang diperoleh dianalisis dengan FT-IR dan XRD. La2O3 yang terbentuk digunakan sebagai katalis dalam reaksi kondensasi aldol antara furfural (F) dan siklopentanon (CP). Reaksi dilakukan dengan variasi rasio reaktan, jumlah katalis, suhu dan waktu reaksi. Produk berupa F2CP dan FCP yang dihasilkan dianalisis dengan GC-MS. Stabilitas katalis diuji dengan menganalisis produk yang dihasilkan dari penggunaan ulang katalis pada berbagai kondisi perlakuan. Berdasarkan hasil penelitian, diperoleh persentase total FCP dan F2CP sebesar 83,793% dari reaksi dengan rasio F:CP = 1:4 mmol pada suhu reaksi 80 derajat Celsius selama 3 jam yang dikatalisis oleh 0,5 mmol La2O3. Aktivitas La2O3 pada reaksi kondensasi aldol setelah reaksi dapat dipulihkan setelah katalis dikalsinasi pada suhu 650 derajat Celsius.

Synthesis of 2-(2-furylmethylidene)cyclopentanone (FCP) and 2,5-bis(2-furylmethylidene)cyclopentanone (F2CP) through aldol condensation reaction has been successfully carried out using prepared La2O3 as a catalyst. The purposes of this study were to prepare La2O3 catalyst through the precipitation method, to analyze the stability of La2O3 as a catalyst on the aldol condensation reaction, to synthesis FCP and F2CP and determine the optimum conditions for the aldol condensation reaction catalyzed by La2O3. La2O3 is one of the heterogeneous catalyst which has a strong basicity that potential to replace the homogeneous catalyst that widely used in the previous aldol condensation reaction. The La2O3 catalyst was prepared using precipitation method. Lanthanum oxide (La2O3) was dissolved in HNO3 and distilled water and NaOH was added dropwise until it reached pH 12. The formed solid was filtered and washed until it reached neutral pH. The La2O3 solid was dried and calcined at 650 degrees Celsius for 3 hours. The catalysts obtained were analyzed by FT-IR and XRD. The La2O3 solid was used as a catalyst in the aldol condensation reaction between furfural (F) and cyclopentanone (CP). The reaction was carried out with a variation of reactant ratio, reaction temperature, catalyst amount and reaction time. The F2CP and FCP products were analyzed by GC-MS. The stability of the catalyst was also studied. Based on the research results, the total product percentage of FCP and F2CP was 83.793% of the reaction with the ratio of F:CP = 1:4 mmol at a reaction temperature of 80 degrees Celsius for 3 h with the catalyst load of 0,5 mmol. The performance of La2O3 in the aldol condensation reaction regained after the spend catalyst was calcined at 650 degrees Celsius.

Kata Kunci : furfural, kondensasi aldol, La2O3, presipitasi, siklopentanon/ aldol condensation, cyclopentanone, furfural, La2O3, precipitation

  1. S1-2021-414634-abstract.pdf  
  2. S1-2021-414634-bibliography.pdf  
  3. S1-2021-414634-tableofcontent.pdf  
  4. S1-2021-414634-title.pdf