Adsorpsi Coomassie Brilliant Blue dengan Nanopartikel Alginat-Kitosan

JIHAN ARLIA PUTRI, Dr.rer.nat. Adhitasari Suratman, M.Si., Drs. Roto, M.Eng., Ph.D.

2021 | Skripsi | S1 KIMIA

Studi adsorpsi coomassie brilliant blue (CBB) dengan nanopartikel alginat-kitosan telah dilakukan. Studi ini bertujuan untuk membuat nanopartikel alginat-kitosan sebagai adsorben untuk mengadsorp CBB, mempelajari pengaruh pH, massa adsorben, waktu kontak, dan konsentrasi awal CBB terhadap kemampuan nanopartikel alginat-kitosan dalam mengadsorp CBB, dan mempelajari kinetika dan isoterm adsorpsi CBB dengan nanopartikel alginat-kitosan. Penelitian ini dilakukan dengan mensintesis nanopartikel alginat-kitosan dengan membuat emulsi alginat-kitosan kemudian diteteskan natrium tripolifosfat (TPP) dan CaCl2. CBB sebelum dan sesusah adsorpsi di uji absorbansinya dengan spektrofotometer UV-Vis. Nanopartikel kemudian dikarakterisasi dengan spektrofotometer inframerah (FT-IR), Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM), dan Zetasizer. Hasil yang diperoleh dari penelitian ini yaitu nanopartikel alginat-kitosan mampu mengadsorp dengan kapasitas adsorpsi sebesar 14,90 mg/g pada pH 2, massa teradsorp sebesar 0,45 mg dengan massa adsorben 0,05 g, kapasitas adsorpsi sebesar 9,58 mg/g pada waktu kontak 90 menit, dan kapasitas adsorpsi sebesar 53,25 mg/g pada konsentrasi awal adsorbat 100 ppm. Nanopartikel alginat kitosan merupakan serbuk berwarna putih gading memiliki permukaan kasar dengan ukuran rata-rata 50,62 nm. Proses adsorpsi zat warna CBB mengikuti kinetika orde dua semu dan mengikuti model isoterm Dubinin-Radushkevich.

The adsorption studies of coomassie brilliant blue (CBB) have been carried out by alginate-chitosan nanoparticles. The purposes of this study are to synthesize alginate-chitosan nanoparticles as an adsorbent to adsorp CBB, analyze the effect of pH, adsorbent mass, contact time, and the initial concentration of the adsorbate on the ability of alginate-chitosan nanoparticles to adsorb CBB, and study the kinetics and adsorption isotherm model of CBB adsorption by alginate-chitosan nanoparticles. This research was performed by synthesizing alginate-chitosan nanoparticles by making an alginate-chitosan emulsion then dropped with sodium tripolyphosphate and CaCl2. CBB before and after adsorbed were analyzed for their absorbance using a UV-Vis spectrophotometer. The nanoparticles were characterized by an infrared spectrophotometer (FT-IR), Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM), and Zetasizer. The results obtained from this study were that the alginate-chitosan nanoparticles were able to adsorb CBB with a maximum adsorption capacity of 14.90 mg/g at pH 2, the adsorbed mass was 0.45 mg at a mass of 0.05 g, a maximum adsorption capacity of 9.58 mg/g at the contact time of 90 min, and a maximum adsorption capacity of 53.25 mg/g at the initial concentration of 100 ppm adsorbate. Alginate-chitosan nanoparticles were ivory white powder that has a rough surface with an average size of 50.62 nm. The adsorption process of CBB followed pseudosecond order kinetics and the Freundlich isotherm model.

Kata Kunci : adsorpsi, alginat, coomassie brilliant blue, kitosan, nanopartikel