ADSORPSI ION LOGAM Ni2+ PADA MANIK ASAM HUMAT-ALGINAT-KITOSAN

DICKY MUHAMMAD ALFIN, Drs. Dwi Siswanta, M.Eng., Ph.D. ; Prof. Drs. Mudasir, M.Eng., Ph.D.

2021 | Skripsi | S1 KIMIA

Adsorpsi ion logam Ni2+ pada manik asam humat-alginat-kitosan telah dilakukan. Sintesis manik asam humat-alginat-kitosan dilakukan pada perbandingan komposisi 1:1:1, 1:2:1, 1:4:1 dan 1:8:1. Manik yang telah disintesis dilakukan uji stabilitasnya terhadap pH, uji penyerapan air dan dikarakterisasi dengan menggunakan FTIR dan SEM-EDX. Kajian adsorpsi dilakukan untuk menentukan komposisi optimum, pH larutan optimum, waktu kontak optimum dan konsentrasi adsorbat yang optimum. Kajian desorpsi dilakukan untuk mempelajari pengaruh variasi larutan pendesorp dan variasi waku desorpsi. Karakterisasi manik asam humat-alginat-kitosan dengan FTIR menunjukkan adanya gugus fungsi -OH, -COOH, dan -NH2. Citra SEM-EDX memperlihatkan tekstur, morfologi dan komposisi unsur pada permukaan manik. Kapasitas adsorpsi optimum ion logam Ni2+ diperoleh sebesar 50,85 mg g-1 pada komposisi manik asam humat-alginat-kitosan dengan rasio 1:8:1 dalam waktu kontak selama 210 menit dengan konsentrasi awal adsorbat 250 mg L-1 pada pH 5. Pada penelitian ini desorpsi ion logam Ni2+ menunjukkan persen desorpsi tertinggi sebesar 81% dalam waktu 1 jam dengan menggunakan larutan HNO3 0,1 M.

The adsorption of Ni2+ metal ions on humic acid-alginate-chitosan beads was studied. Synthesis of the humic acid-alginate-chitosan beads was carried out with a composition rasio 1:1:1, 1:2:1, 1:4:1, and 1:8:1. The synthesized bead was tested for stability against pH, water absorption test and characterized using FTIR and SEM-EDX. The adsorption study carried out to determine the optimum composition, the optimum pH of the solution, the optimum contact time and the optimum adsorbate concentration. Desorption studied were carried by studying the effect of variations in the desorbent solution and variations in the time of desorption. The FTIR characterization of the humic acid-alginate-chitosan beads showed the presence of -OH, -COOH, and -NH2 functional groups. The SEM-EDX image showed the texture, morphology and elemental composition of the bead surface. The optimum adsorption capacity of Ni2+ metal ions was obtained at 50.85 mg g-1 in the composition of humic acid-alginate-chitosan beads with a ratio of 1:8:1 at contact time of 210 min with an adsorbate initial concentration of 250 mg L-1 and pH 5. In this study, Ni2+ metal ions desorption showed the highest percentage of desorption of 81% within 1 hour using a 0.1 M HNO3 solution.

Kata Kunci : adsorpsi, alginat, asam humat, desorpsi, kitosan