DEGRADASI ZAT WARNA LIMBAH BATIK LENDAH KULONPROGO DENGAN ELEKTRODA PbO2 TERDOPING NIKEL

NAUFA SALSABILA S, Drs. Roto, M.Eng., Ph.D.; Dr. Agus Kuncaka, DEA.

2021 | Skripsi | S1 KIMIA

Pada penelitian ini elektroda PbO2 dimodifikasi dengan metode elektrolisis. PbO2 didoping dengan enam ion logam yang berbeda yaitu Mg2+, Co2+, Cu2+, Ni2+, Ag2+, Zn2+ serta diujikan pada elektrodegradasi zat warna metilen biru. Keenam elektroda PbO2 yang telah didoping tersebut kemudian dikarakterisasi dengan XRD dan FTIR dan diujikan ke zat warna metilen biru untuk melihat logam yang paling baik dalam mendegradasi zat warna tersebut. Anoda yang terbaik kemudian digunakan untuk mendegradasi sampel limbah batik pada waktu, konsentrasi NaCl, dan kerapatan arus listrik yang telah dioptimasi. Hasil penelitian menunjukkan bahwa anoda PbO2-Ni paling efektif dalam mendegradasi zat warna metilen biru daripada anoda lainnya. Keberadaan nikel di permukaan elektroda membantu meningkatan kinerja PbO2 sebagai anoda. Elektrolisis menggunakan anoda PbO2-Ni selama 30 menit dengan pH 8, konsentrasi NaCl 0,075 M, serta kerapatan arus listrik 20 mA/cm2 memberikan persen degradasi limbah A sebesar 24,95% dan limbah B sebesar 43,81%.

In this study, PbO2 electrodes were modified by the electrolysis method. PbO2 was doped with six different metal ions that were Mg2+, Co2+, Cu2+, Ni2+, Ag+, and Zn2+ and were tested on electrochemical degradation of methylene blue. The six PbO2 electrodes that have been doped were characterized by XRD and FTIR and tested on methylene blue degradation to understand the best metal for degrading the dye. The best anode was used to degrade samples of batik waste at the optimized time, NaCl concentration, and current density. The results showed that the PbO2-Ni electrode is the most effective in degrading methylene blue than other electrodes. The presence of nickel on the surface of the electrodes helps improve the performance of PbO2 as an anode. Electrolysis using PbO2-Ni anode for 30 minutes in pH 8, NaCl concentration of 0.075 M, and electric current density of 20 mA/cm2 give percent degradation of waste A of 24.95% and waste B of 43.81%, respectively.

Kata Kunci : degradasi elektrokimia, PbO2, PbO2-Ni, limbah batik

  1. S1-2021-394140-abstract.pdf  
  2. S1-2021-394140-bibliography.pdf  
  3. S1-2021-394140-tableofcontent.pdf  
  4. S1-2021-394140-title.pdf