Degradasi Fotokatalitik Methylene Blue (MB) menggunakan Nanopartikel Magnetik CoZn-Fe2O4/SiO2

APRINANDA NAFLA AULIA HANIFAH, Dr.Eng. Edi Suharyadi, S.Si., M.Eng.

2021 | Skripsi | S1 FISIKA

Nanopartikel magnetik CoZn-Fe2O4 disintesis dengan metode kopresipitasi. Selanjutnya nanopartikel berhasil dienkapsulasi dengan SiO2 menggunakan metode Stober untuk memodifikasi permukaan nanopartikel CoZn-Fe2O4 agar meningkatkan aktivitas fotokatalitiknya. Nanopartikel CoZn-Fe2O4/SiO2 dengan variasi konsentrasi larutan SiO2 yaitu 0%, 10%, 20%, 30%, dan 50% dikarakterisasi menggunakan X-ray diffraction (XRD), Transmission Electron Microscopy (TEM) dan UV-Visible spectrophotometer. Dari hasil karakterisasi menunjukkan bahwa nanopartikel magnetik CoZn-Fe2O4/SiO2 berhasil disintesis. Aktivitas fotokatalitk dari nanopartikel magnetik core/shell CoZn-Fe2O4/SiO2 dalam mendegradasi methylene blue (MB) dibawah sinar UV juga diamati. Seluruh sampel menunjukkan efisiensi degradasi MB meningkat tajam dan maksimum pada interval waktu 0 hingga 30 menit. Setelah fotodegradasi selama 30 menit, persentase degradasi untuk nanopartikel tanpa shell adalah 86,2% sedangkan setelah enkapsulasi SiO2 50% menjadi 96,7%. Dibandingkan dengan nanopartikel CoZn-Fe2O4 tanpa enkapsulasi, nanopartikel core/shell CoZn-Fe2O4/SiO2 menunjukkan aktivitas fotokatalitik yang lebih baik terutama pada variasi enkapsulasi 50%.

Magnetic nanoparticles (MNPs) CoZn-Fe2O4 were synthesized using co-precipitation method. Subsequently, MNPs were successfully encapsulated with SiO2 using Stober method to modify the surface of CoZn-Fe2O4 MNPs and to increase the photocatalytic activity. Prepared CoZn-Fe2O4/SiO2 with concentrations of SiO2 solution varied from 0%, 10%, 20%, 30%, and 50% were characterized using X-ray diffraction (XRD), Transmission Electron Microscopy (TEM), and UV-Visible spectrophotometer. It was found that the CoZn-Fe2O4/SiO2 MNPs were successfully obtained. Photocatalytic activity of core/shell structured CoZn-Fe2O4/SiO2 MNPs in degrading methylene blue (MB) dye under UV-light irradiation was observed. The results show that the maximum degradation efficiency for all the samples occurred in the first 30 minutes. The degradation of methylene blue after 30 minutes for MNPs without shell was 86.2% and for the encapsulated sample (SiO2 50%) was 96.7%. Compared with CoZn-Fe2O4 MNPs, core/shell structured CoZn-Fe2O4/SiO2 MNPs show better photocatalytic activity, especially for the encapsulation 50%.

Kata Kunci : photocatalytic degradation, core/shell, methylene blue degradation, cobalt zinc ferrite magnetic nanoparticles, silica.

  1. S1-2021-412587-abstract.pdf  
  2. S1-2021-412587-bibliography.pdf  
  3. S1-2021-412587-tableofcontent.pdf  
  4. S1-2021-412587-title.pdf