Laporkan Masalah

HIDRORENGKAH MINYAK NYAMPLUNG (Calophyllum inophyllum L.) MENJADI BIOFUEL MENGGUNAKAN KATALIS MONO-, BI-, DAN TRIMETAL DENGAN VARIASI LOGAM Ni, Co, Mo, TERIMPREGNASI PADA GAMMA Al2O3

MESAKH T. W. BOIKH, Prof. Dra. Wega Trisunaryanti, M.S., Ph.D.Eng; Prof. Dr. rer. nat. Karna Wijaya, M.Eng

2020 | Tesis | MAGISTER KIMIA

Telah dilakukan preparasi katalis mono, bi, dan trimetal logam Ni, Co, dan Mo yang diembankan pada γ-Al2O3 menggunakan metode impregnasi basah untuk hidrorengkah minyak nyamplung menjadi biofuel. Tujuan penelitian ini adalah mempelajari pengaruh variasi logam yang diembankan pada γ-Al2O3, suhu, dan rasio katalis umpan terhadap aktivitas katalitik dan selektivitas katalis dalam proses hidrorengkah minyak nyamplung menjadi biofuel. Material katalis hasil sintesis diberi label sebagai Ni/γ-Al2O3; Co/γ-Al2O3; Mo/γ-Al2O3; NiMo/γ-Al2O3; CoMo/γ-Al2O3; NiCo/γ-Al2O3; dan NiCoMo/γ-Al2O3. Hasil penelitian menunjukkan bahwa pengembanan logam Ni, Co, and Mo pada γ-Al2O3 mampu menaikkan nilai keasaman katalis dan menurunkan luas permukaan, volume pori serta diameter pori γ-Al2O3. Katalis NiCoMo/γ-Al2O3 memiliki aktivitas katalitik terbaik dibanding katalis lainnya dengan menghasilkan produk cair 71,64% b/b dengan selektivitas fraksi bensin 60,84% b/b serta fraksi solar sebesar 5,39% b/b. Sementara itu, suhu 550 °C merupakan suhu optimum yang dapat digunakan pada proses hidrorengkah. Uji variasi katalis umpan menggunakan katalis Co/γ-Al2O3 menghasilkan produk cair 61,31% b/b menggunakan rasio katalis umpan 1:100 dan selektivitas tertinggi menggunakan variasi katalis umpan 1:200 dengan persentase fraksi bensin 47,08% b/b, katalis bimetal CoMo/γ-Al2O3 menghasilkan produk cair 70,83% b/b dengan variasi katalis umpan 1:300 sementara selektivitas tertinggi menggunakan variasi katalis umpan 1:200 dengan persentase fraksi bensin 56,02% b/b. Katalis trimetal NiCoMo/γ-Al2O3 menghasilkan produk cair sebanyak 75,84% b/b menggunakan variasi katalis umpan 1:200 dengan tingkat selektivitas fraksi bensin 70,80% b/b.

The preparation of mono-, bi-, and trimetallic catalysts has been carried out by using the wet impregnation method with a variation of nickel, cobalt, and molybdenum precursors impregnated in γ-Al2O3 material. The purpose of this study is to investigate the effect of metal-bearing variations on the catalyst, catalytic activity, and selectivity in the hydrocracking of nyamplung oil into biofuel. The obtained catalyst materials were labelled as Co/γ-Al2O3; Mo/γ-Al2O3; NiMO/γ-Al2O3; CoMo/γ-Al2O3; NiCo/γ-Al2O3; and NiCoMo/γ-Al2O3. The impregnation process of Ni, Co, and Mo metals was able to increase the acidity of the catalyst and reduce the surface area, pore-volume, and pore diameter of γ-Al2O3. NiCoMo/γ-Al2O3 catalyst has the best catalytic activity compared to other catalysts by producing 71.64% w/w liquid product with the selectivity of 60.84% w/w for gasoline fraction and 5.39% w/w of diesel fraction. Meanwhile, the temperature of 550 °C is the optimum temperature that can be used in the hydrocracking. The variation test of the feed catalyst using the Co/γ-Al2O3 catalyst produced 61.31% w/w liquid product using a 1:100 ratio of feed catalyst and the highest selectivity using a variation of the feed catalyst 1:200 produced 47.08% w/w gasoline fraction, CoMo/γ-Al2O3 produced a liquid product of 70.83% w/w with a variation of the feed catalyst 1:300, while the highest selectivity used a variation of 1:200 feed catalyst with a percentage of 56.02% w/w gasoline fraction. The NiCoMo/γ-Al2O3 tri-metallic catalyst produced 75.84% w/w liquid product using a 1: 200 variation of the feed catalyst with a selectivity level of 70.80% w/w gasoline fraction.

Kata Kunci : hidrorengkah, katalis, biofuel, gamma Al2O3, minyak nyamplung

  1. S2-2020-433831-Abstract.pdf  
  2. S2-2020-433831-Bibliography.pdf  
  3. S2-2020-433831-Tableofcontent.pdf  
  4. S2-2020-433831-Title.pdf