SITI AISAH, Prof. Dr. Sri juari santosa, M.Eng; Dr. Sutarno, M.Si.

2020 | Tesis | MAGISTER KIMIA

Pada penelitian ini telah dipelajari imobilisasi asam galat (AG) pada Ni-Zn LHS dan aplikasinya untuk adsorpsi-reduksi [AuCl4]-. Sintesis Ni-Zn LHS dilakukan dengan metode kopresipitasi menggunakan perbandingan molar Ni(NO3)2 dan Zn(NO3)2 sebesar 2:1 serta NaOH 0,75 M sebanyak 14 mL. Pada proses imobilisasi asam galat dan adsorpsi-reduktif [AuCl4]-, dikaji pengaruh pH terhadap proses imobilisasi dan model isoterm adsorpsi. Keberhasilan imobilisasi asam galat pada Ni-Zn LHS dan aplikasinya untuk adsorpsi-reduktif [AuCl4]- dibuktikan dengan karakterisasi menggunakan FTIR, XRD, dan SEM-EDX. Hasil penelitian menunjukkan bahwa proses imobilisasi asam galat pada Ni-Zn LHS optimum pada pH 5 dan mengikuti model isoterm Freundlich dengan nilai KF 10,65 mg g-1. Spektra FTIR AG-Ni-Zn LHS menunjukkan keberadaan puncak serapan pada bilangan gelombang 1474 cm-1 yang merupakan vibrasi gugus C=C dari asam galat terimobilisasi. Proses adsorpsi [AuCl4]- oleh AG-Ni-Zn LHS optimum pada pH 3 dan cenderung mengikuti isoterm Freundlich dengan nilai KF sebesar 11,33 mg g-1. Hasil karakterisasi AG-Ni-Zn LHS menggunakan XRD menunjukkan bahwa adsorpsi-reduksi [AuCl4]- berhasil dilakukan dengan munculnya karakteristik logam Au pada d111, d200, d220, dan d311 secara berurutan di 2teta¸ 2,37; 2,05; 1,44; dan 1,23.

This research studied gallic acid (AG) immobilization on Ni-Zn LHS and its application for reductive adsorption of [AuCl4]-. Synthesis of Ni-Zn LHS used coprecipitation method with molar ratio Ni(NO3)2:Zn(NO3)2 (2:1) and 14 mL of NaOH 0.75 M. In the procces of immobilization of gallic acid and reductive adsorption of [AuCl4]-, the effect of pH and isotherm adsorption were also studied. The success of gallic acid immobilization on Ni-Zn LHS and its application for reductive adsorption of [AuCl4]- were confirmed by FTIR, XRD, and SEM-EDX. The results showed the immobilization of gallic acid on Ni-Zn LHS was optimum at pH 5 and followed the Freundlich isotherm with a KF value of 10.65 mg g-1. The FTIR spectra of AG-Ni-Zn LHS showed the peak at 1474 cm-1 which was vibration of C=C from gallic acid immobilized. The adsorption process of [AuCl4]- on AG-Ni-Zn-LHS was optimum at pH 3 and tended to follow the Freundlich isotherm with a KF value of 11.33 mg g-1. Characterization of AG-Ni-Zn LHS with XRD showed reductive adsorption of [AuCl4]- has been success with the appearance of gold peaks at d111, d200, d220, and d311 which coresponded to 2theta¸ 2.37; 2.05; 1.44; and 1.23.

Kata Kunci : Ni-Zn LHS, asam galat, emas, adsorpsi-reduktif/Ni-Zn LHS, gallic acid, gold, reductive adsorption

  1. S2-2020-418596-abstract.pdf  
  2. S2-2020-418596-bibliography.pdf  
  3. S2-2020-418596-tableofcontent.pdf  
  4. S2-2020-418596-title.pdf