PENGARUH pH PREPARASI TiO2/SiO2-ABU VULKANIK TERHADAP AKTIVITAS FOTOKATALIS PADA OKSIDASI AMONIA DALAM LARUTAN

DYAH SETYANINGRUM, Prof. Dr. Endang Tri Wahyuni, M. S.;Prof. Dr. Mudasir, M.Eng.

2016 | Tesis | S2 Ilmu Kimia

Telah dilakukan preparasi dan karakterisasi fotokatalis TiO2/SiO2 serta uji aktivitasnya untuk fotooksidasi amonia. Preparasi fotokatalis dilakukan dengan cara menginteraksikan larutan titanium tetraisopropoksida (TTIP) dengan SiO2 gel dari abu vulkanik pada pH yang bervariasi, yaitu 2, 4, 6, dan 9. Untuk mengetahui pengaruh pengembanan TiO2 pada SiO2 dilakukan karakterisasi dengan menggunakan metode XRD, FTIR, dan SEM. Fotokatalis TiO2/SiO2 selanjutnya diuji aktivitasnya pada fotooksidasi amonia dalam larutan. Pada proses fotooksidasi amonia, dipelajari pengaruh pH preparasi TiO2/SiO2, massa fotokatalis, dan pH amonia dalam larutan terhadap efektivitas fotooksidasi. Hasil penelitian menunjukkan bahwa pengembanan TiO2 pada SiO2 gel dapat menurunkan ukuran partikel TiO2, sehingga memberikan aktivitas fotokatalis yang lebih tinggi (34,74%) dibandingkan TiO2 (7,19%). Uji aktivitas fotokatalis pada fotooksidasi amonia yang tertinggi diperoleh dengan menggunakan fotokatalis TiO2/SiO2 yang dipreparasi pada pH 4. Pada proses fotooksidasi amonia dalam larutan, kenaikan massa fotokatalis TiO2/SiO2 sampai 30 mg dapat meningkatkan efektivitas fotooksidasi amonia mencapai 50,70%. Kondisi optimum fotooksidasi amonia dalam larutan diperoleh pada pH 7, yaitu sebesar 50,80%.

Preparation and characterization of TiO2/SiO2 photocatalyst using SiO2 gel from Kelud volcanic ash and its activity test in ammonia photooxidation have been conducted. Preparation of photocatalyst was carried out by mixing titanium tetraisopropoksida (TTIP) with SiO2 gel at various pH, ie 2, 4, 6, and 9. To determine the impregnation effect of TiO2 in SiO2, characterizations of the material were performed by using XRD, FTIR, and SEM methods. TiO2/SiO2 photocatalyst activity was tested for photooxidation of aqueous ammonia. In the photooxidation of ammonia, the effect of preparation pH of TiO2/SiO2, mass of photocatalyst, and the pH of the aqueous ammonia also have been systematically investigated. The results of the research indicated that impregnation of TiO2 in SiO2 decreased the particle size of TiO2, thus providing higher photocatalytic activity (34.74%) as compared to TiO2 (7.19%). The photocatalytic activity obtained the highest photooxidation of aqueous ammonia by using TiO2/SiO2 prepared at pH 4. In the photooxidation of aqueous ammonia, the increase mass of TiO2/SiO2 photocatalyst up to 30 mg improved the effectiveness of ammonia up to 50.70%. Optimum photooxidation of aqueous ammonia was 50.80% at pH 7.

Kata Kunci : Abu vulkanik, TiO2/SiO2, amonia dalam larutan, fotookidasi/ Volcanic ash, TiO2/SiO2, ammonia in solution, photooxidation