Laporkan Masalah

STUDI PEMBUATAN BETON RINGAN NON AAC (Non Autoclaved Aerated Concrete) DENGAN BAHAN TAMBAH HIDROGEN PEROKSIDA, MILL DAN FLYASH 1 BAGI 1

GANGSAR PERMADI, Lava Himawan, S.T., M.T.

2017 | Tugas Akhir | D3 TEKNIK SIPIL SV

Perkembangan dunia konstruksi di Indonesia ikut mendorong betambahnya penggunaan beton sebagai material perkuatan struktur. Bata ringan saat ini dikenal ada 2 (dua) jenis yaitu Autoclaved Aerated Concrate (AAC) dan Celluler Lightweight (CLC). CLC sering disebut juga beton Non AAC (Autoclaved Aerated Concrate). Dimana beton yang dimatangkan tanpa autoclave ini belum banyak dikomersialkan dibanding beton ringan AAC. Penelitian ini di titik beratkan pada hasil kuat tekan, dan porositas. Beton ringan yang di pakai penelitian ini adalah Non AAC (Autoclaved Aerated Concrate) dengan bahan penyusun yang meliputi air, pasir, semen mill, cairan pengeras SikaCim, dan Hidrogen peroksida. Dengan focus pada metode pengadukan yang sangat berpengaruh pada hasil 4 uji trial, kemudian ditetapkan pada trial ke 4 sebagai benda uji dan koefisien Water/cement (w/c): 0,40, Sand/Cement ( s/c ): 0.75, H2O2:0.1, mill/ Cement (%): 0.5. Kemudian pengujian yang dilakukan yaitu uji kuat tekan ,porositas dan uji berat jenis. Pada hasil uji kuat tekan campuran beton ringan yang berjumlah 9 eksperimen rata-rata nilai kuat terkan tertinggi diperoleh pada BRD-06 dengan nilai 2,47 MPa. Dan rata-rata nilai kuat tekan terendah di peroleh pada eksperimen BRD-09 yaitu 1,79 MPa. Porositas tertinggi didapat pada eksperimen BRD-01 dengan nilai 22,47% dan porositas terendah di dapat pada eksperimen BRD-06 dengan nilai 15,04%. Hasil rata-rata nilai berat jenis dengan nilai tertinggi di dapat dari eksperimen BRD-06 yaitu dengan nilai 1083,7 kg/m3 dan nilai terendah diperoleh oleh eksperimen BRD-01 dengan nilai 923,7 kg/m3.

The development of construction in Indonesia contributes to the increasing use of concrete as a structural reinforcement material. There are two types of light brick known so far; Autoclaved Aerated Concrete (AAC) and Cellular Lightweight (CLC). CLC is often referred to Non AAC (autoclaved Aerated Concrete) as it has not been widely commercialized compared to the lightweight AAC. This study focused on the results of compressive strength and porosity. Lightweight concrete used in this study was the Non AAC (autoclaved Aerated Concrete) which the constituent material includes water, sand, cement mill, liquid hardener SikaCim, and hydrogen peroxide. With the focus on the method of stirring which is very influential to the results of four test trials, then the fourth trial was set as a test object and a coefficient of water / cement (w / c): 0,40, Sand / Cement (s / c): 0.75, H2O2 : 0.1, mill / Cement (%): 0.5. Then test of the compressive strength, porosity and density test was done. In the test results of compressive strength of lightweight concrete mixtures which consist of 9 experiments, the average highest compressive strength value was obtained at BRD-06 with a value of 2,47 MPa. The average value of the lowest compressive strength obtained in experiments BRD-09 was 1,79 MPa. The highest porosity was obtained in experiments BRD-01 with a value of 22,47% and lowest porosity was obtained in the experiment BRD-06 with a value of 15,04%. The average specific gravity value with the highest values was obtained from experiment BRD-06 with the value of 1083,7 kg / m3 and the lowest value was obtained in the experiments BRD-01 with a value of 923,7 kg / m3.

Kata Kunci : Hidrogenperoksida, beton ringan, Non ACC

  1. D3-2017-327955-abstract.pdf  
  2. D3-2017-327955-bibliography.pdf  
  3. D3-2017-327955-tableofcontent.pdf  
  4. D3-2017-327955-title.pdf