Laporkan Masalah

PENGARUH APLIKASI NOVAMIN DALAM PASTA GIGI DAN METODE ETSA TERHADAP KEKUATAN TARIK PELEKATAN BRAKET EDGEWISE PADA PERMUKAAN EMAIL GIGI

DWI AGUSTINA, drg. Christnawati, M.Kes., Sp.Ort (K)

2015 | Tesis | SP ORTODONSIA

Novamin (calcium sodium phosphosilicate) dalam pasta gigi yang terpapar saliva akan membentuk lapisanhydroxicarbonate apatiteberfungsi melindungi gigi terhadap asam. Pengetsaan permukaan email gigi dapat dilakukan dengan etch and rinseatauself etching primer. Penelitian ini bertujuan untuk mempelajari pengaruh aplikasi Novamin dan jenis etsa terhadap kekuatan tarik braket Edgewise pada permukaan email gigi. Penelitian in vitro ini dilakukan pada 20 gigi premolar yang dibagi secara acak menjadi 2 kelompok (Novamin dan tanpa Novamin), masing-masing kelompok dibagi lagi menjadi sub kelompok (etch and rinse dan self etching primer). Aplikasi pasta gigi dilakukan pada semua gigi selama 5 hari.Setiap selesai penyikatan gigi direndam dalam saliva buatan pH 6,7. Selanjutnya dilakukan pelekatan braket dan pengukuran kekuatan tarik dengan menggunakan Universal Testing Mechine. Uji ARI (Adhesive Remnant Index) digunakan untuk mengetahui letak kegagalan pelekatan braket. Analisis statistik yang digunakan adalah Uji Anava dua jalur dan Uji chi-square. Hasil penelitian menunjukkan bahwa kekuatan tarik pelekatan braket Edgewise antara kelompok Novamin dengankelompok tanpa Novamin serta antara kelompok etch and rinse dengan kelompok self etching primer terdapat perbedaan yang sangat bermakna (p<0,01), kecuali interaksi kelompok aplikasi Novamin dan jenis etsa (p>0,05). Kesimpulan dari penelitian ini adalah kekuatan tarik pelekatan braket pada permukaan email gigi menjadi lebih rendah karena pengaruh Novamin, sedangkan padaetch and rinsemenjadi lebih tinggi. Letak kegagalan pelekatan braket setelah aplikasi Novamin dan self etching primersebagian besar terjadi antara permukaan email dan bahan pelekat. Kata kunci : Novamin, etch and rinse, self etching primer, uji kekuatan tarik, uji ARI (Adhesive Remnant Index)

Novamin (calcium sodium phosphosilicate) in toothpaste exposed to saliva will form hydroxicarbonate apatite layer serves to protect the teeth against acid. Etching the enamel surface can be performed with etch and rinse or self etching primer. The purpose of this reseacrch was to figure out the effect of Novamin’s applicationand the type of etching at tensile strength of Edgewise bracket on the enamel surface. This study was in vitro research, conducted on 20 premolars were randomly divided into two groups (Novamin and without Novamin), each group was subdivided into groups (etch and rinse and selfetching primer). Application toothpaste to all the teeth for 5 days. Each teeth was brushed than immersed in artificial saliva pH 6.7. Bracket application and the tensile strength was measured by Universal Testing Mechine and ARI (Adhesive Remnant Index). Data collections were analysed by ANOVA and chi-square test . The results showed that the tensile strength of edgewise bracket adhesion between the groups Novamin and without Novamin and between groups of etch and rinse with self etching primer were highly significant difference (p<0.01), exept the interaction of group application Novaminand etch type (p>0.05). The conclusion is the tensile strength of attachment bracket on the enamel surface will be lower due to the influence of Novamin, while the etch and rinse becomes higher. Location of attachment bracket failure after application and self etching primer Novamin mostly occurs between the enamel surface and adhesive materials. Keywords: Novamin, etch and rinse, selfetching primer, tensile strength, ARI (Adhesive Remnant Index)

Kata Kunci : Novamin, etch and rinse, self etching primer, uji kekuatan tarik, uji ARI (Adhesive Remnant Index); Novamin, etch and rinse, selfetching primer, tensile strength, ARI (Adhesive Remnant Index)


    Tidak tersedia file untuk ditampilkan ke publik.