Laporkan Masalah

ANALISA CACAT INKLUSI TERAK DAN POROSITY PADA PRODUK CASTING PRESSURE PLATE PP MX1 DI PT. AT INDONESIA

DEBY ALWI KUSUMA, Lilik Dwi Setyana, ST., MT.

2016 | Tugas Akhir | D3 TEKNIK MESIN SV

PT. AT Indonesia merupakan perusahaan yang bergerak di bidang casting, machining yang mensuplai produk otomotif maupun non otomotif di dalam negeri maupun diluar negeri. Adapun produk yang dihasilkan oleh perusahaan ini antara lain flywheel, exhaust manifold, disc rotor, brake drum, body caliper, knuckle steering, pressure plate dan lain-lain. Dalam dunia industri pengecoran logam jika terdapat kesalahan pada produk pengecoran harus dilakukan perbaikan agar target produksi dapat tercapai dibawah 5%. Salah satu produk yang memerlukan perbaikan di PT. AT Indonesia adalah produk pressure plate PP MX1 pada ACE line-1. Improvement diperlukan karena produk not good (NG) yang terkena cacat inklusi terak dan porosity ditemukan saat produksi pada proses machining. Tujuan dari Tugas Akhir ini adalah untuk mengurangi persentase produk NG sesuai standar perusahaan. Improvement yang dilakukan setelah menganalisa produk pressure plate PP MX1 yang terkena cacat inklusi terak adalah dengan menambah sistem penjebakan pada sistem alir pattern pressure plate PP MX1. Untuk menganalisa produk pressure plate PP MX1 yang terkena cacat porosity adalah dengan menurunkan prosentase level maksimum carbon equivalent (CE) yang sebelumnya 4.79 % menjadi 4.60 %. Perubahan tersebut bertujuan untuk mengurangi cacat porosity yang terjadi pada produk pressure plate PP MX1 karena proses solidification time butuh waktu lama. Setelah dilakukan improvement, cacat inklusi terak dan cacat porosity yang ditemukan pada produk pressure plate PP MX1 berkurang. Nilai reject relatif yang awalnya pada bulan januari sampai februari sebesar 19.84 - 23.58% berkurang menjadi 8.0 – 1.60 % pada bulan maret sampai april 2016. Dengan berkurangnya nilai reject relatif, improvement yang dilakukan telah berhasil mengurangi persentase produk NG.

PT. AT Indonesia is a company engaged in the field of casting, machining supplying the automotive and non-automotive products in the country or abroad. The products produced by this company, among others flywheel, exhaust manifold, disc rotor, brake drum, body caliper, knuckle steering, pressure plate and others. On foundry industrial manufacturing, if there is a failure in casting products should be improved so that production targets can be achieved below 5%. One of product that require improvement on PT. AT Indonesia is the product pressure plate PP MX1 on 1st ACE line. Improvement very needed because NG (no good) product are exposed reject slag inclusion and porosity was found during production in the machining process. The purpose of this final task for reduce the percentage of NG (not good) product to achieve the company target. The improvement that is applied after analyzing the product pressure plate PP MX1 are exposed reject slag inclusion with add trapping at gating system pattern pressure plate PP MX1. For analyzing product of pressure plate PP MX1 that is exposed reject porosity is to decrease the percentage of the maximum level of carbon equivalent (CE) previously 4.79% to 4.60%. The change is made to reduce reject porosity that has happened on product pressure plate PP MX1 because processing of solidification time need a long time. After improvement has applied, reject slag inclusion and reject porosity that is found on product pressure plate PP MX1 diminish. Value reject relative that was beginning in January to February amounted to 19.84% – 23.58% reduced to 8.0% - 1.60% in March to April 2016. With diminish of value reject relative, the improvement undertaken has succeeded in reducing the percentage of NG products.

Kata Kunci : Cacat inklusi terak, cacat porosity, NG produk