STUDI ADSORPSI DAN DESORPSI REDUKTIF PADA PEMBENTUKAN NANOPARTIKEL EMAS DARI PRINTED CIRCUIT BOARDS

ROKIY ALFANAAR, Prof. Dr. Sri Juari Santosa, M. Eng

2015 | Tesis | S2 Ilmu Kimia

Telah dilakukan sintesis nanopartikel emas dari limbah printed circuit boards(PCB) dengan proses adsorpsi menggunakan Mg/Al hidrotalsit dan desorpsi reduktif menggunakan natrium sitrat dan asam glutamat. Penelitian pertama kali diawali dengan mengurangi kandungan logam tidak berharga dari PCB menggunakan metode asam oksidator ganda dengan larutan campuran H2O2 30%-H2SO4 3 M pada perbandingan volume 3:1 dan waktu pelindian 3 hari. Logam Cu yang terlepas setelah pelindian sebesar 25449 mg/L (254,49 mg Cu/g PCB). Proses kedua adalah pelarutan logam Au dengan aqua regia yang dibantu dengan gelombang mikro dan mampu melepas emas sebesar 137 mg/L (1,37 mg Au/g PCB). Emas hasil pelindian diadsorpsikan pada Mg/Al hidrotalsit dan dilanjutkan dengan desorpsi menggunakan NaOH 0,5 M. Emas hasil desorpsi selanjutnya direduksi untuk menghasilkan nanopartikel emas dengan menggunakan agen pembatas natrium sitrat dan asam glutamat. Surface plasmon resonance maksimum nanopartikel emas diperoleh pada konsentrasi natrium sitrat 60 mM dan asam glutamat 80 mM.

Gold nanoparticles have been synthesis from waste printed circuit boards (PCB) through process of adsorption using Mg/Al hydrotalcite and reductive desorption using sodium citrate and glutamatic acid. The research was first initiated by reducing the content of non-precious metals from PCB using double oxidation-acid leaching method with a mixed solution of H2O2 30%-H2SO4 3 M at a volume ratio of 3: 1 and the time of leaching 3 days. The Cu metal released after leaching as 25449 mg/L (254.49 mg Cu/g PCB). The second process was microwave assisted-aqua regia leaching for Au and it was able to leach Au 137 mg/L (1.37 mg Au/g PCB). The leached Au was adsorbed to Mg / Al hydrotalcite and followed by desorption using 0.5 M NaOH. The desorbed Au was then reduced to produce gold nanoparticles by using sodium citrate and glutamic acid as capping agent. Maximum surface plama resonance of gold nanoparticles was obtained at concentrations of sodium citrate 60 mM and glutamate 80 mM.

Kata Kunci : nanopartikel emas, printed circuit boards¸Mg/Al Hydrotalcite


    Tidak tersedia file untuk ditampilkan ke publik.