Telah dilakukan penelitian tentang pemanfaatan Tomografi Komputer untuk pengujian kualitas logam kuningan. Tujuan penelitian adalah mengkaji kemampuan sistem Tomografi Komputer dengan sumber radiasi isotop I131 untuk memetakan perbedaan kualitas beberapa tipe logam kuningan. Dalam penelitian ini, juga dikaji pengaruh besar aktivitas isotop I131 terhadap citra hasil rekonstruksi. Pengujian dilakukan dengan cara pemayaran terhadap tiga tipe logam kuningan, serta dibandingkan dengan logam Cu dan Zn, yang merupakan bahan utama penyusun kuningan. Penentuan kualitas kuningan diidentifikasi berdasarkan profil serapan radiasi, distribusi nilai koefisien atenuasi linear (μ) pada citra, dan kontras citra, sedangkan hasil yang diperoleh dibandingkan dengan hasil temuan menggunakan program simulasi XCOM. Pengaruh besar aktivitas isotop I131 dikaji berdasarkan tampilan sinogram dan citra hasil rekonstruksi. Hasil analisis terhadap data hasil penelitian menunjukkan bahwa kuningan berkualitas baik mempunyai serapan radiasi yang lebih besar dibandingkan kuningan kualitas yang kurang baik, yang direpresentasikan oleh nilai μ yang besar. Dari pengamatan secara visual terhadap citra hasil rekonstruksi diperoleh bahwa semakin tinggi aktivitas isotop I131 yang digunakan dalam proses pemayaran, kontras sinogram dan kontras citra rekonstruksi yang dihasilkan makin tajam.

A research on application of computed tomography to quality inspection of brass alloy has been done. The aim of the research was to study capability of computed tomography system with source radiation isotope I131 in order to mapping different quality of any type of brass alloy. In this research, a study on the influence of activity of isotope I131 to the reconstructed image has been done. The inspection has been done by scanning three type of brass alloy, and comparing to the Cu and Zn metals which are the fundamental substances of brass alloy. The quality of brass alloy was identified through the profile of absorption of radiation and the distribution value of linear coefficient attenuation (μ) on the image and image contrast, while those results were compared to the result of the XCOM simulation program. The influence of activity isotope I131 was studied by performance through the sinogram and reconstructed image. The result showed that the good quality of brass alloy have highest absorption of radiation than that of the bad quality of brass alloy, which were represented by the higher value of μ. From the visual observation on the reconstructed image, it showed that the higher activity of isotope I131 would be used on the scanning process, the sharper sinogram contrast and reconstructed image contrast.

Kata Kunci : Tomografi Komputer,Radiasi Isotop I,Kualitas Logam Kuningan, computed tomography, isotope, brass alloy, absorption of radiation